ABSTRACT
We report continuous-wave (CW) blue semipolar (202¯1) III-nitride laser diodes (LDs) that incorporate limited area epitaxy (LAE) n-AlGaN bottom cladding with thin p-GaN and ZnO top cladding layers. LAE mitigates LD design limitations that arise from stress relaxation, while ZnO layers reduce epitaxial growth time and temperature. Numerical modeling indicates that ZnO reduces the internal loss and increases the differential efficiency of TCO clad LDs. Room temperature CW lasing was achieved at 445 nm for a ridge waveguide LD with a threshold current density of 10.4 kA/cm2, a threshold voltage of 5.8 V, and a differential resistance of 1.1 Ω.
ABSTRACT
Incorporating transparent conducting oxide (TCO) top cladding layers into III-nitride laser diodes (LDs) improves device design by reducing the growth time and temperature of the p-type layers. We investigate using ZnO instead of ITO as the top cladding TCO of a semipolar (202¯1) III-nitride LD. Numerical modeling indicates that replacing ITO with ZnO reduces the internal loss in a TCO clad LD due to the lower optical absorption in ZnO. Lasing was achieved at 453 nm with a threshold current density of 8.6 kA/cm2 and a threshold voltage of 10.3 V in a semipolar (202¯1) III-nitride LD with ZnO top cladding.