Comparative Evaluation of the Repair Bond Strength of Dental Resin Composite after Sodium Bicarbonate or Aluminum Oxide Air-Abrasion.

The dental prophylactic cleaning of a damaged resin-based composite (RBC) restoration with sodium bicarbonate can change the surface characteristics and influence the repair bond strength. The purpose of this study was to compare the effect of sodium bicarbonate (SB) and aluminum oxide (AO) surface treatments on the microtensile bond strength (µTBS) of repaired, aged RBC. Bar specimens were prepared from microhybrid RBC and aged in deionized water for 8 weeks. Different surface treatments (AO air-abrasion; SB air-polishing), as well as cleaning (phosphoric acid, PA; ethylene-diamine-tetraacetic-acid, EDTA) and adhesive applications (single bottle etch-and-rinse, ER; universal adhesive, UA), were used prior to the application of the repair RBC. Not aged and aged but not surface treated RBCs were used as positive and negative controls, respectively. The repaired blocks were cut into sticks using a precision grinding machine. The specimens were tested for tensile fracture and the µTBS values were calculated. Surface characteristics were assessed using scanning electron microscopy. AO-PA-UA (62.6 MPa) showed a 20% increase in µTBS compared to the NC (50.2 MPa), which proved to be the most significant. This was followed by SB-EDTA-UA (58.9 MPa) with an increase of 15%. In addition to AO-PA-UA, SB-EDTA-UA could also be a viable alternative in the RBC repair protocol.

Effect of Air-Polishing and Different Post-Polishing Methods on Surface Roughness of Nanofill and Microhybrid Resin Composites.

Air-abrasion is a popular prophylactic procedure to maintain oral hygiene. However, depending on the applied air-abrasive powder, it can damage the surface of the tooth and restorations, making it susceptible to plaque accumulation. The purpose of this study was to investigate the effect of 5 s and 10 s air-abrasion of calcium carbonate on surface roughness (Ra) of enamel, nanofill, and microhybrid resin-composites and the effect of post-polishing with two-step rubber- (RP) or one-step brush polisher (BP) to re-establish the surface smoothness. Surface topography was visualized by scanning-electron-microscopy. The quantitative measurement of the Ra was carried out with atomic-force-microscopy. Air-abrasion for 10 s decreased the Ra of enamel as a result of abrasion of the natural surface texture. Post-polishing with RP after 10 s air-abrasion did not change the Ra or BP; however, Ra was increased significantly by scratching the surface. Air-abrasion increased the Ra of resin composites significantly, irrespective of the application time. While RP provided a similarly smooth surface to the control in the case of microhybrid resin composite, BP increased the Ra significantly. The Ra for the control group of the nanofill-resin composite was initially high, which was further increased by air-abrasion. RP and BP re-established the initial Ra with deeper and shallower scratches after BP. Both the material and treatment type showed a large effect on Ra.