ABSTRACT
Loosening and infection are the main reasons for revision surgery in total hip arthroplasty (THA). Removing partially detached cemented implant components during revision surgery remains challenging and poses the risk of periprosthetic bone damage. A promising approach for a gentler removal of partially detached prostheses involves softening the PMMA-based bone cement by heating it above its glass transition temperature (TG), thus loosening the implant-cement bond. It is assumed that the TG of PMMA-based bone cement decreases in-vivo due to the gradual absorption of body fluid. Reliable data on TG are essential to develop a heat-based method for removing cemented implant components during revision surgery. The effect of water absorption was investigated in-vitro by ageing PMMA-based bone cement samples for different periods up to 56 days in both Ringer's solution (37 °C) and air (37 °C and 30% humidity). Subsequently, the TG and Vicat softening temperatures of the samples were determined by differential scanning calorimetry and Vicat tests, respectively, according to prescribed methods. Over the entire ageing period, i.e. comparing one day of ageing in air and 56 days in Ringer's solution, the Vicat softening temperature dropped by 16 °C, while the TG dropped by 10 °C for Palacos® R PMMA-based bone cement. Water absorption over time correlated significantly with the Vicat softening temperature until saturation of the PMMA-based bone cement was reached. Based on the TG and Vicat softening temperature measurements, it can be assumed that in body-aged bone cement, an optimal softening can be achieved within a temperature range of 85 °C-93 °C to loosen the bond between the PMMA-based bone cement mantle and the prosthesis stem. These findings may pave the way for a gentler removal of the implant in revision THA.
Subject(s)
Arthroplasty, Replacement, Hip , Hip Prosthesis , Arthroplasty, Replacement, Hip/methods , Bone Cements/chemistry , Polymethyl Methacrylate/chemistry , Reoperation/methods , Ringer's Solution , WaterABSTRACT
Within the framework of the Collaborative Research Center 1153, we investigated novel process chains for the production of bulk components with different metals as joining partners. In the present study, the co-extrusion of coaxially reinforced hollow profiles was employed to manufacture semi-finished products for a subsequent die-forging process, which was then used for the manufacture of hybrid bearing bushings. The hybrid hollow profiles, made of the aluminum alloy EN AW-6082 paired with either the case-hardening steel 20MnCr5, the stainless steel X5CrNi18-10, or the rolling bearing steel 100Cr6, were produced by Lateral Angular Co-Extrusion. Push-out tests on hybrid hollow sections over the entire sample cross-section showed shear strengths of 44 MPa ± 8 MPa (100Cr6) up to 63 MPa ± 5 MPa (X5CrNi18-10). In particular, the influence of force and form closure on the joint zone could be determined using specimen segments tested in shear compression. Locally, shear strengths of up to 131 MPa (X5CrNi18-10) were demonstrated in the shear compression test. From these samples, lamellae for microstructural analysis were prepared with a Focused Ion Beam. Detailed analyses showed that for all material combinations, a material bond in the form of an ultra-thin intermetallic phase seam with a thickness of up to 50 nm could be established.
ABSTRACT
Fringe projection profilometry in combination with other optical measuring technologies has established itself over the last decades as an essential complement to conventional, tactile measuring devices. The non-contact, holistic reconstruction of complex geometries within fractions of a second in conjunction with the lightweight and transportable sensor design open up many fields of application in production metrology. Furthermore, triangulation-based measuring principles feature good scalability, which has led to 3D scanners for various scale ranges. Innovative and modern production processes, such as sheet-bulk metal forming, thus, utilize fringe projection profilometry in many respects to monitor the process, quantify possible wear and improve production technology. Therefore, it is essential to identify the appropriate 3D scanner for each application and to properly evaluate the acquired data. Through precise knowledge of the measurement volume and the relative uncertainty with respect to the specimen and scanner position, adapted measurement strategies and integrated production concepts can be realized. Although there are extensive industrial standards and guidelines for the quantification of sensor performance, evaluation and tolerancing is mainly global and can, therefore, neither provide assistance in the correct, application-specific positioning and alignment of the sensor nor reflect the local characteristics within the measuring volume. Therefore, this article compares fringe projection systems across various scale ranges by positioning and scanning a calibrated sphere in a high resolution grid.
ABSTRACT
To investigate ductile damage in parts made by cold sheet-bulk metal forming a suited specimen preparation is required to observe the microstructure and defects such as voids by electron microscopy. By means of ion beam slope cutting both a targeted material removal can be applied and mechanical or thermal influences during preparation avoided. In combination with scanning electron microscopy this method allows to examine voids in the submicron range and thus to analyze early stages of ductile damage. In addition, a relief structure is formed by the selectivity of the ion bombardment, which depends on grain orientation and microstructural defects. The formation of these relief structures is studied using scanning electron microscopy and electron backscatter diffraction and the use of this side effect to interpret the microstructural mechanisms of voids formation by plastic deformation is discussed. A comprehensive investigation of the suitability of ion beam milling to analyze ductile damage is given at the examples of a ferritic deep drawing steel and a dual phase steel.