ABSTRACT
In this study, the carburization characteristics of cast and cold-rolled CoCrFeMnNi high-entropy alloys (HEAs) with various grain sizes were investigated. All specimens were prepared by vacuum carburization at 940 °C for 8 h. The carburized/diffused layer was mainly composed of face-centered cubic structures and Cr7C3 carbide precipitates. The carburized/diffused layer of the cold-rolled specimen with a fine grain size (~1 µm) was thicker (~400 µm) than that of the carburized cast specimen (~200 µm) with a coarse grain size (~1.1 mm). In all specimens, the carbides were formed primarily through grain boundaries, and their distribution varied with the grain sizes of the specimens. However, the carbide precipitates of the cast specimen were formed primarily at the grain boundaries and were unequally distributed in the specific grains. Owing to the non-uniform formation of carbides in the carburized cast specimen, the areas in the diffused layer exhibited various carbide densities and hardness distributions. Therefore, to improve the carburization efficiency of equiatomic CoCrFeMnNi HEAs, it is necessary to refine the grain sizes.