ABSTRACT
A high-quality buffer layer serves as one of the most significant issues that influences the efficiency of solar cells. Doping in semiconductors is an important strategy that can be used to control the reaction growth. In this study, the influence of Ag doping on the morphological, optical and electrical properties of CdS thin films have been obtained. Herein, we propose the mechanism of CdS film formation with and without Ag ions, and we found that changes in the reaction of preparing CdS by the chemical bath deposition (CBD) method cause a shift in the geometric composition of the CdS film. XRD showed that the position of peaks in the doped films are displaced to wider angles, indicating a drop in the crystal lattice constant. The optical analysis confirmed direct transition with an optical energy gap between 2.10 and 2.43 eV. The morphological studies show conglomerates with inhomogeneously distributed spherical grains with an increase of the Ag ratio. The electrical data revealed that the annealed Ag-doped CdS with 5% Ag has the highest carrier concentration (3.28 × 1015 cm-3) and the lowest resistivity (45.2 Ω cm). According to the results, the optimal Ag ratio was obtained at Ag 5%, which encourages the usage of CdS in this ratio as an efficient buffer layer on photovoltaic devices.
ABSTRACT
[This corrects the article DOI: 10.1039/D2RA04790J.].
ABSTRACT
The aim of this study is to acquire a deeper understanding of the response mechanism that is associated with the formation of CdS thin films. We presented an effective and new hybrid sensitisation technique, which involved the 1-step linker between the related chemical bath deposition (CBD) process and the traditional doping method during CBD for synthesising high-quality, CdS thin films. The mechanism for the combined synthesis of the films is also describes. CdS films were electrostatically bonded to soda-lime glass, causing the formation of the intermediate complexes [Cd(NH3)4]2+, which aided in the collision of these complexes with a soda-lime glass slide. In the one-step fabrication technique, 3-Mercaptopropionic Acid (MPA) was employed as a second source of sulphur ions and a linker molecule. Optical studies showed that the bandgap ranged between (2.26-2.52) eV. CdS + MPA films exhibited a uniform distribution of spherical molecules based on their morphological properties. After annealing, this approach significantly altered the electrical characteristics of CdS films. The CdS + MPA films displayed the highest carrier concentration whereas the CdS + Ag + MPA films exhibited the lowest resistivity, with a jump of 3 orders of magnitude.
ABSTRACT
In this study, we aimed to increase the knowledge regarding the response mechanisms which were associated with the formation of CdS thin films. CdS thin film remains the most appealing alternative for many researchers, as it has been a capable buffer material for effect in film based polycrystalline solar cells (CdTe, CIGSe, CZTS). The Linker Assisted and Chemical Bath Deposition (LA-CBD) technique, which combines the Linker Assisted (LA) technique and the chemical bath deposition (CBD) method for forming high quality CdS thin film, was presented as an efficient and novel hybrid sensitization technique. CdS films were bound to soda lime with the help of electrostatic forces, which led to the formation of the intermediate complexes [Cd (NH3)4]2+ that helped in the collision of these complexes with a soda lime slide. Salvia dye and as a linker molecule 3-Mercaptopropionic acid (MPA) was used in the one step fabrication technique. Optical results showed that the bandgap varied in the range of (2.50 to 2.17) eV. Morphological properties showed a homogeneous distribution of the particles that aspherical in shape in the CdS + MPA + Salvia dye films. This technique significantly affected on the electrical characterizations of CdS films after the annealing process. The CdS + Ag + MPA + Salvia dye films showed the maximum carrier concentration and minimum resistivity, as 5.64 × 10 18 cm-3 and 0.83 Ω cm respectively.