Properties of natural rubber reinforced with cellulose nanofibers based on fiber diameter distribution as estimated by differential centrifugal sedimentation.

Cellulose nanofibers (CNFs) with different degrees of fibrillation are prepared by the mechanical fibrillation of kraft pulp using wet disk milling, and dispersions of the prepared CNFs were subjected to differential centrifugal sedimentation (DCS) in order to estimate the diameter distributions of the CNFs. The low-fibrillated CNFs (fiber diameter (d): >10 µm) had a weak reinforcing effect on natural rubber (NR), while the medium-fibrillated CNFs (d: 0.1-10 µm) dramatically improve the initial modulus and decrease the elongation at break. The high-fibrillated CNFs (d: <0.1 µm) enhanced the tensile strength even further while maintaining the elongation at break. The reinforcing mechanism of the NR composites reinforced by the CNFs (NR-CNFs) was confirmed by field-emission scanning electron microscopy imaging, dynamic mechanical analysis, and toluene uptake measurements. It was concluded that these characteristic mechanical properties of the NR-CNFs were determined by the morphologies of the CNFs. The branching structure of the medium-fibrillated CNFs affected high improvement of the initial modulus, and the network formed by the high-fibrillated CNFs were involved in enhancement of the tensile strength without compromising viscoelastic properties. Understanding the effect of their diameter distribution can potentially reduce the production cost of CNFs and thus expand their applicability.

Drastic Improvement in Adhesion Property of Polytetrafluoroethylene (PTFE) via Heat-Assisted Plasma Treatment Using a Heater.

The heating effect on the adhesion property of plasma-treated polytetrafluoroethylene (PTFE) was examined. For this purpose, a PTFE sheet was plasma-treated at atmospheric pressure while heating using a halogen heater. When plasma-treated at 8.3 W/cm2 without using the heater (Low-P), the surface temperature of Low-P was about 95 °C. In contrast, when plasma-treated at 8.3 W/cm2 while using the heater (Low-P+Heater), the surface temperature of Low-P+Heater was controlled to about 260 °C. Thermal compression of the plasma-treated PTFE with or without heating and isobutylene-isoprene rubber (IIR) was performed, and the adhesion strength of the IIR/PTFE assembly was measured via the T-peel test. The adhesion strengths of Low-P and Low-P+Heater were 0.12 and 2.3 N/mm, respectively. Cohesion failure of IIR occurred during the T-peel test because of its extremely high adhesion property. The surfaces of the plasma-treated PTFE with or without heating were investigated by the measurements of electron spin resonance, X-ray photoelectron spectroscopy, nanoindentation, scanning electron microscopy, and scanning probe microscopy. These results indicated that heating during plasma treatment promotes the etching of the weak boundary layer (WBL) of PTFE, resulting in a sharp increase in the adhesion property of PTFE.