Optimizing Hard Carbon Anodes from Agricultural Biomass for Superior Lithium and Sodium Ion Battery Performance.

Biomass-derived carbon materials are gaining attention for their environmental and economic advantages in waste resource recovery, particularly for their potential as high-energy materials for alkali metal ion storage. However, ensuring the reliability of secondary battery anodes remains a significant hurdle. Here, we report Areca Catechu sheath-inner part derived carbon (referred to as ASIC) as a high-performance anode for both rechargeable Li-ion (LIBs) and Na-ion batteries (SIBs). We explore the microstructure and electrochemical performance of ASIC materials synthesized at various pyrolysis temperatures ranging from 700 to 1400 °C. ASIC-9, pyrolyzed at 900 °C, exhibits multilayer stacked sheets with the highest specific surface area, and the least lateral size and stacking height. ASIC-14, pyrolyzed at 1400 °C, demonstrates the most ordered carbon structure with the least defect concentration and the highest stacking height and an increased lateral size. ASIC-9 achieves the highest capacities (676 mAh/g at 0.134C) and rate performance (94 mAh/g at 13.4C) for hosting Li+ ions, while ASIC-14 exhibits superior electrochemical performance for hosting Na+ ions, maintaining a high specific capacity after 300 cycles with over 99.5% Coulombic efficiency. This comprehensive understanding of structure-property relationships paves the way for the practical utilization of biomass-derived carbon in various battery applications.

Developing High-Performance In-Plane Flexible Aqueous Zinc-Ion Batteries with Laser-Scribed Carbon-Supported All Electrodeposited Electrodes.

Developing high-performance, safer, and affordable flexible batteries is of urgent need to power the fast-growing flexible electronics market. In this respect, zinc-ion chemistry employing aqueous-based electrolytes represents a promising combination considering the safety, cost efficiency, and both high energy and high-power output. Herein, we represent a high-performance flexible in-plane aqueous zinc-ion miniaturized battery constructed with all electrodeposited electrodes, i.e., MnO2 cathode and zinc anode with polyimide-derived interdigital patterned laser-scribed carbon (LSC) as the current collector as well as the template for electrodeposition. The LSC possesses a cross-linked network of graphitic carbon sheet, which offers large surface area over low footprint and ensures active materials loading with a robust conductive network. The LSC with high zincophilic characteristic also offers dendrite-free zinc deposition with very low Zn2+ plating stripping overpotential. Benefitting from the Zn//MnO2-rich redox chemistry, the ability of the 3D LSC network to uniformly distribute reaction sites, and the architectural merits of in-plane interdigitated electrode configuration, we report very high capacity values of ∼549 mAh/g (or ∼523 µAh/cm2) and 148 mAh/g (or 140 µAh/cm2) at 0.1 A/g (0.095 mA/cm2) and 2 A/g (1.9 mA/cm2) currents, respectively. The device was also able to maintain a high capacity of 196 mAh/g (areal capacity of 76.19 µAh/cm2) at 1 A/g (0.95 mA/cm2) current after 1350 cycles. The flexibility of the device was demonstrated in polyacryl amide (PAM) gel polymer soaked with a 2 M ZnSO4 and 0.2 M MnSO4 electrolyte, which exhibited a comparable specific capacity of ∼102-110 mAh/g in flat condition and different bending (100° or 160° bending) conditions. The device does not use any conventional current collector, separator, and conductive or polymer additives. The overall process is highly scalable and can be completed in less than a couple of hours.