ABSTRACT
Heterodimeric nanoparticles comprising materials with different functionalities are of great interest for fundamental research and biomedical/industrial applications. In this work, Fe3O4-Au nano-heterostructures were synthesized by a one-step thermal decomposition method. The hybrid nanoparticles comprise a highly crystalline 12 nm magnetite octahedron decorated with a single noble metal sphere of 6 nm diameter. Detailed analysis of the nanoparticles was performed by UV-visible spectroscopy, magnetometry, calorimetry and relaxometry studies. The cytotoxic effect of the nanoparticles in the human hepatic cell line Huh7 and PLC/PRF/5-Alexander was also assessed. These Fe3O4-Au bifunctional nanoparticles showed no significant cytotoxicity in these two cell lines. The nanoparticles showed a good theranostic potential for liver cancer treatment, since the r2 relaxivity (166.5 mM-1·s-1 and 99.5 mM-1·s-1 in water and HepG2 cells, respectively) is higher than the corresponding values for commercial T2 contrast agents and the Specific Absorption Rate (SAR) value obtained (227 W/gFe) is enough to make them suitable as heat mediators for Magnetic Fluid Hyperthermia. The gold counterpart can further allow the conjugation with different biomolecules and the optical sensing.
ABSTRACT
The chemical synthesis of nanoparticles with a preassigned size and shape is important for an optimized performance in any application. Therefore, systematic monitoring of the synthesis is required for the control and detailed understanding of the nucleation and growth of the nanoparticles. Here, we study Fe3O4-Au hybrid nanoparticles in detail using probes of the reaction mixture during synthesis and their thorough characterization. The proposed approach eliminates the problem of repeatability and reproducibility of the chemical synthesis and was carried out using laboratory equipment (standard transmission electron microscopy, X-ray diffraction, and magnetometry) for typically 10 µL samples instead of, for example, a dedicated synthesis and inspection at a synchrotron radiation facility. From the three independent experimental techniques we extract the nanoparticle size at 12 stages of the synthesis. These diameters show identical trends and good quantitative agreement. Two consecutive processes occur during the synthesis of Fe3O4-Au nanoparticles, the nucleation and the growth of spherical Fe3O4 nanoparticles on the surface of Au seeds during the heating stage and their faceting towards octahedral shape during reflux. The final nanoparticles with sizes of 15 nm Fe3O4 and 4 nm Au exhibit superparamagnetic behavior at ambient temperature. These are high-quality, close to stoichiometric Fe3O4 nanocrystals with nearly volumetric magnetic behavior as confirmed by the presence of the Verwey transition. Understanding the processes occurring during the synthesis allows the nanoparticle size and shape to be adjusted, improving their capabilities in biomedical applications.
Subject(s)
Ferrosoferric Oxide/chemistry , Gold/chemistry , Magnetite Nanoparticles/chemistry , Ferrosoferric Oxide/chemical synthesis , Particle Size , Surface PropertiesABSTRACT
Magnetic hyperthermia (MHT) is a promising approach for cancer therapy. However, a systematic MHT characterization as function of temperature on the therapeutic efficiency is barely analyzed. Here, we first perform comparative temperature-dependent analysis of the cobalt ferrite nanoparticles-mediated MHT effectiveness in two murine tumors models - breast (4T1) and colon (CT26) cancer in vitro and in vivo. The overall MHT killing capacity in vitro increased with the temperature and CT26 cells were more sensitive than 4T1 when heated to 43 °C. Well in line with the in vitro data, such heating cured non-metastatic CT26 tumors in vivo, while only inhibiting metastatic 4T1 tumor growth without improving the overall survival. High-temperature MHT (>47 °C) resulted in complete 4T1 primary tumor clearance, 25-40% long-term survival rates, and, importantly, more effective prevention of metastasis comparing to surgical extraction. Thus, the specific MHT temperature must be defined for each tumor individually to ensure a successful antitumor therapy.
Subject(s)
Breast Neoplasms/therapy , Cell Proliferation/drug effects , Colonic Neoplasms/therapy , Magnetic Field Therapy , Animals , Breast Neoplasms/pathology , Cell Line, Tumor , Cell Survival/drug effects , Cobalt/chemistry , Cobalt/pharmacology , Colonic Neoplasms/pathology , Disease Models, Animal , Female , Ferric Compounds/chemistry , Ferric Compounds/pharmacology , Humans , Hyperthermia, Induced/methods , Magnetite Nanoparticles/chemistry , Magnetite Nanoparticles/therapeutic use , Mice , Neoplasm Metastasis , TemperatureABSTRACT
Size-selected Fe3O4-Au hybrid nanoparticles with diameters of 6-44 nm (Fe3O4) and 3-11 nm (Au) were prepared by high temperature, wet chemical synthesis. High-quality Fe3O4 nanocrystals with bulk-like magnetic behavior were obtained as confirmed by the presence of the Verwey transition. The 25 nm diameter Fe3O4-Au hybrid nanomaterial sample (in aqueous and agarose phantom systems) showed the best characteristics for application as contrast agents in magnetic resonance imaging and for local heating using magnetic particle hyperthermia. Due to the octahedral shape and the large saturation magnetization of the magnetite particles, we obtained an extraordinarily high r 2-relaxivity of 495 mM-1·s-1 along with a specific loss power of 617 W·gFe -1 and 327 W·gFe -1 for hyperthermia in aqueous and agarose systems, respectively. The functional in vitro hyperthermia test for the 4T1 mouse breast cancer cell line demonstrated 80% and 100% cell death for immediate exposure and after precultivation of the cells for 6 h with 25 nm Fe3O4-Au hybrid nanomaterials, respectively. This confirms that the improved magnetic properties of the bifunctional particles present a next step in magnetic-particle-based theranostics.