ABSTRACT
Polyacrylonitrile (PAN) fibers are widely used as precursors in the manufacture of high-conducting and mechanically resistant carbon fibers. The modulation of such fibers is carried out through electrospinning. In this work, we show the production and control of the morphology of nanometric-range PAN fibers for their potential use as precursors for high-electrical-conductivity carbon fibers. PAN samples dissolved in dimethylformamide (DMF) were prepared at 6, 10, and 12% w/w, at 15 and 25 kV. The impact of the rotation of the collector drum at 100, 300, and 500 RPM was also studied. It was found that the percentage of PAN in the solution proportionally affects the diameter of the fibers and that the preparation potential affects the morphology. The rotation speed, when increased, decreases the diameter, and it has a negative impact on the morphology. Fibers prepared with 6% w/w at 15 kV and 500 RPM show 90 nm diameters, the smallest diameter of all the samples.
ABSTRACT
Gallium (Ga) ion-doped TiO2 (Ga-TiO2) nanocomposite with small particle size (9-10 nm) and high surface area (104 m2/g) has been easily synthesized via sol-gel method at low temperature by using low-valent GaI as a doping precursor. The structural and morphological characterization of Ga-TiO2 was carried out with standard analytical and spectroscopic techniques. Ga doping into the TiO2 matrix inhibited a phase transformation from anatase to rutile (photocatalytically inactive) form, even at a higher temperature of 750 °C. Finally, Ga-TiO2 nanocomposite showed high photocatalytic activity and exhibited 97% degradation of acid violet 63 dye within 60 min. The dye degradation rate constant was calculated as 1.6 × 10-1 and 1.4 × 10-1 min-1 under UV and white light irradiation, respectively, which is higher, as compared to the previously reported Ga-TiO2 composites to date.