A comparative study of acid-treated, base-treated, and Fenton-like reagent-treated biomass for Cr(VI) sequestration from aqueous solutions.

A wide variety of biomass materials have been used for the removal of toxic chromium(VI) by biosorption. The current study investigated the efficacy of Macadamia nutshells treated with sodium hydroxide, nitric acid, and the Fenton-like reagent in the removal of Cr(VI). The adsorbents were characterized by FTIR, SEM, TGA, and elemental analysis. Effects of functional parameters influencing the adsorption of Cr(VI), solution pH (pH 1-11), contact time (5-250 min), concentration of adsorbent (1-10 g/L), and adsorbate concentration (10-200 mg/L) were investigated. The optimum conditions for biosorption were pH 1.4, adsorbent dose of 5 g/L, and 160 min of contact time. In all cases, the base-treated adsorbent displayed superior performance compared to others, with highest percent removal of 98%. The adsorbate-adsorbent interactions were better explained by the Freundlich isotherm and the pseudo-first-order rate model. The Macadamia-based adsorbents are potentially useful for Cr(VI) removal from aqueous solutions. PRACTITIONER POINTS: Three different chemical activators were investigated for the modification of Macadamia surface. The base-treated material exhibited the highest specific surface area of 12.1 m2 /g. The Cr(VI) adsorption performance for the base-treated material dwarfed the other materials. Excellent Cr(VI) removal efficiency in the presence of competitors was achieved.

Evaluating the Effect of Varying the Metal Precursor in the Colloidal Synthesis of MoSe2 Nanomaterials and Their Application as Electrodes in the Hydrogen Evolution Reaction.

Herein we report on the use of different metal precursors in the synthesis of MoSe2 nanomaterials in order to control their morphology. The use of Mo(CO)6 as the metal precursor resulted in the formation of wrinkled few-layer nanosheets, while the use of H2MoO4 as the metal precursor resulted in the formation of nanoflowers. To investigate the effect of the morphologies on their performance as catalysts in the hydrogen evolution reaction, electrochemical characterization was done using linear sweep voltammetry (LSV), cyclic voltammetry (CV), and electrical impedance spectroscopy (EIS). The MoSe2 nanoflowers were found to have superior electrochemical performance towards the hydrogen evolution reaction with a lower Tafel slope, on-set potential, and overpotential at 10 mA/cm2 compared to the wrinkled few-layer nanosheets. This was found to be due to the higher effective electrochemical surface area of the nanoflowers compared to the nanosheets which suggests a higher number of exposed edge sites in the nanoflowers.