Stereochemical Heterogeneity Analysis of Polylactides by Multidimensional Liquid Chromatography.

A new and robust high-performance liquid chromatography (HPLC) method that separates poly(lactic acid) (PLA) according to its stereochemical composition is presented. Using this method, poly(l-lactide) incorporating trace amounts of meso-lactide resulting from the racemization is separated from the pristine polymer. To prove this aspect in more detail, a representative poly(l-lactic acid) standard, assumed to be highly homogeneous, was separated using this method. The result showed that this was not the case as a fraction incorporating meso-lactide due to racemization occurring during the synthesis is separated. Employing two-dimensional liquid chromatography (2D-LC), the molar mass differences of the separated species were investigated, and fractions with similar molecular sizes were detected, confirming that the LC separation is solely based on stereochemical heterogeneity. The sample was further fractionated by preparative HPLC, followed by an in-depth analysis of the fractions using homonuclear decoupling in proton nuclear magnetic resonance (1H NMR). Convincing results that unveiled significant differences in the stereochemistry of the isolated PLA fractions were obtained. Subsequent analysis by matrix-assisted laser desorption ionization time-of-flight mass spectrometry (MALDI-TOF-MS) also confirmed oligomer series with different end group structures, indicating that the applied HPLC method is very sensitive to minor variations in stereochemistry and end groups. This integrated approach offers detailed insight into the structural characteristics of PLA polymers, contributing to a better understanding of their composition and potential applications.

Lignin, the Lignification Process, and Advanced, Lignin-Based Materials.

At a time when environmental considerations are increasingly pushing for the application of circular economy concepts in materials science, lignin stands out as an under-used but promising and environmentally benign building block. This review focuses (A) on understanding what we mean with lignin, i.e., where it can be found and how it is produced in plants, devoting particular attention to the identity of lignols (including ferulates that are instrumental for integrating lignin with cell wall polysaccharides) and to the details of their coupling reactions and (B) on providing an overview how lignin can actually be employed as a component of materials in healthcare and energy applications, finally paying specific attention to the use of lignin in the development of organic shape-memory materials.

Iron(ii) carboxylates and simple carboxamides: an inexpensive and modular catalyst system for the synthesis of PLLA and PLLA-PCL block copolymers.

The combination of inexpensive Fe(ii) acetate with low molecular weight aliphatic carboxamides in situ generates an effective catalyst system for the ring opening polymerisation of lactones. PLLAs were produced in melt conditions with molar masses of up to 15 kg mol-1, narrow dispersity (D = 1.03), and without racemisation. The catalytic system was investigated in detail with regard to Fe(ii) source, and steric and electronic effects of the amide's substituents. Furthermore, the synthesis of PLLA-PCL block copolymers of very low randomness was achieved. This commercially available, inexpensive, modular, and user-friendly catalyst mixture may be suitable for polymers with biomedical applications.

Bio-Inspired Magnetically Controlled Reversibly Actuating Multimaterial Fibers.

Movements in plants, such as the coiling of tendrils in climbing plants, have been studied as inspiration for coiling actuators in robotics. A promising approach to mimic this behavior is the use of multimaterial systems that show different elastic moduli. Here, we report on the development of magnetically controllable/triggerable multimaterial fibers (MMFs) as artificial tendrils, which can reversibly coil and uncoil on stimulation from an alternating magnetic field. These MMFs are based on deformed shape-memory fibers with poly[ethylene-co-(vinyl acetate)] (PEVA) as their core and a silicone-based soft elastomeric magnetic nanocomposite shell. The core fiber provides a temperature-dependent expansion/contraction that propagates the coiling of the MMF, while the shell enables inductive heating to actuate the movements in these MMFs. Composites with mNP weight content ≥ 15 wt% were required to achieve heating suitable to initiate movement. The MMFs coil upon application of the magnetic field, in which a degree of coiling N = 0.8 ± 0.2 was achieved. Cooling upon switching OFF the magnetic field reversed some of the coiling, giving a reversible change in coiling ∆n = 2 ± 0.5. These MMFs allow magnetically controlled remote and reversible actuation in artificial (soft) plant-like tendrils, and are envisioned as fiber actuators in future robotics applications.

Cell-Material Interactions 2022.

Cell-material interactions are the defining feature of biomaterials, and they are relevant for evaluating material residues and pollutants [...].

Establishment of an in vitro thrombogenicity test system with cyclic olefin copolymer substrate for endothelial layer formation.

In vitro thrombogenicity test systems require co-cultivation of endothelial cells and platelets under blood flow-like conditions. Here, a commercially available perfusion system is explored using plasma-treated cyclic olefin copolymer (COC) as a substrate for the endothelial cell layer. COC was characterized prior to endothelialization and co-cultivation with platelets under static or flow conditions. COC exhibits a low roughness and a moderate hydrophilicity. Flow promoted endothelial cell growth and prevented platelet adherence. These findings show the suitability of COC as substrate and the importance of blood flow-like conditions for the assessment of the thrombogenic risk of drugs or cardiovascular implant materials. SUPPLEMENTARY INFORMATION: The online version contains supplementary material available at 10.1557/s43579-021-00072-6.

Soft, Formstable (Co)Polyester Blend Elastomers.

High crystallization rate and thermomechanical stability make polylactide stereocomplexes effective nanosized physical netpoints. Here, we address the need for soft, form-stable degradable elastomers for medical applications by designing such blends from (co)polyesters, whose mechanical properties are ruled by their nanodimensional architecture and which are applied as single components in implants. By careful controlling of the copolymer composition and sequence structure of poly[(L-lactide)-co-(ε-caprolactone)], it is possible to prepare hyperelastic polymer blends formed through stereocomplexation by adding poly(D-lactide) (PDLA). Low glass transition temperature Tg ≤ 0 °C of the mixed amorphous phase contributes to the low Young's modulus E. The formation of stereocomplexes is shown in DSC by melting transitions Tm > 190 °C and in WAXS by distinct scattering maxima at 2θ = 12° and 21°. Tensile testing demonstrated that the blends are soft (E = 12-80 MPa) and show an excellent hyperelastic recovery Rrec = 66-85% while having high elongation at break εb up to >1000%. These properties of the blends are attained only when the copolymer has 56-62 wt% lactide content, a weight average molar mass >140 kg·mol-1, and number average lactide sequence length ≥4.8, while the blend is formed with a content of 5-10 wt% of PDLA. The devised strategy to identify a suitable copolymer for stereocomplexation and blend formation is transferable to further polymer systems and will support the development of thermoplastic elastomers suitable for medical applications.

Thermally-Induced Shape-Memory Behavior of Degradable Gelatin-Based Networks.

Shape-memory hydrogels (SMH) are multifunctional, actively-moving polymers of interest in biomedicine. In loosely crosslinked polymer networks, gelatin chains may form triple helices, which can act as temporary net points in SMH, depending on the presence of salts. Here, we show programming and initiation of the shape-memory effect of such networks based on a thermomechanical process compatible with the physiological environment. The SMH were synthesized by reaction of glycidylmethacrylated gelatin with oligo(ethylene glycol) (OEG) α,ω-dithiols of varying crosslinker length and amount. Triple helicalization of gelatin chains is shown directly by wide-angle X-ray scattering and indirectly via the mechanical behavior at different temperatures. The ability to form triple helices increased with the molar mass of the crosslinker. Hydrogels had storage moduli of 0.27-23 kPa and Young's moduli of 215-360 kPa at 4 °C. The hydrogels were hydrolytically degradable, with full degradation to water-soluble products within one week at 37 °C and pH = 7.4. A thermally-induced shape-memory effect is demonstrated in bending as well as in compression tests, in which shape recovery with excellent shape-recovery rates Rr close to 100% were observed. In the future, the material presented here could be applied, e.g., as self-anchoring devices mechanically resembling the extracellular matrix.

Response of Endothelial Cells to Gelatin-Based Hydrogels.

The establishment of confluent endothelial cell (EC) monolayers on implanted materials has been identified as a concept to avoid thrombus formation but is a continuous challenge in cardiovascular device engineering. Here, material properties of gelatin-based hydrogels obtained by reacting gelatin with varying amounts of lysine diisocyanate ethyl ester were correlated with the functional state of hydrogel contacting venous EC (HUVEC) and HUVEC's ability to form a monolayer on these hydrogels. The density of adherent HUVEC on the softest hydrogel at 37 °C (G' = 1.02 kPa, E = 1.1 ± 0.3 kPa) was significantly lower (125 mm-1) than on the stiffer hydrogels (920 mm-1; G' = 2.515 and 5.02 kPa, E = 4.8 ± 0.8 and 10.3 ± 1.2 kPa). This was accompanied by increased matrix metalloprotease activity (9 pmol·min-2 compared to 0.6 pmol·min-2) and stress fiber formation, while cell-to-cell contacts were comparable. Likewise, release of eicosanoids (e.g., prostacyclin release of 1.7 vs 0.2 pg·mL-1·cell-1) and the pro-inflammatory cytokine MCP-1 (8 vs <1.5 pg·mL-1·cell-1) was higher on the softer than on the stiffer hydrogels. The expressions of pro-inflammatory markers COX-2, COX-1, and RAGE were slightly increased on all hydrogels on day 2 (up to 200% of the control), indicating a weak inflammation; however, the levels dropped to below the control from day 6. The study revealed that hydrogels with higher moduli approached the status of a functionally confluent HUVEC monolayer. The results indicate the promising potential especially of the discussed gelatin-based hydrogels with higher G' as biomaterials for implants foreseen for the venous system.

Formulation of drug-loaded oligodepsipeptide particles with submicron size.

The size of particulate carriers is key to their transport and distribution in biological systems, and needs to be tailored in the higher submicron range to enable follicular uptake for dermal treatment. Oligodepsipeptides are promising nanoparticulate carrier systems as they can be designed to exhibit enhanced interaction with drug molecules. Here, a fabrication scheme for drug-loaded submicron particles from oligo[3-(S)-sec-butylmorpholine-2,5-dione]diol (OBMD) is presented based on an emulsion solvent evaporation method with cosolvent, surfactant, and polymer concentration as variable process parameters. The particle size (300-950 nm) increased with lower surfactant concentration and higher oligomer concentration. The addition of acetone increased the particle size at low surfactant concentration. Particle size remained stable upon the encapsulation of models compounds dexamethasone (DXM) and Nile red (NR), having different physicochemical properties. DXM was released faster compared to NR due to its higher water solubility. Overall, the results indicated that both drug-loading and size control of OBMD submicron particles can be achieved. When applied on porcine ear skin samples, the NR-loaded particles have been shown to allow NR penetration into the hair follicle and the depth reached with the 300 nm particles was comparable to the one reached with the cream formulation. A potential benefit of the particles compared to a cream is their sustained release profile.

Supramolecular Gelatin Networks Based on Inclusion Complexes.

Hydrogel forming physical networks based on gelatin are an attractive approach toward multifunctional biomaterials with the option of reshaping, self-healing, and stimuli-sensitivity. However, it is challenging to design such gelatin-based hydrogels to be stable at body temperature. Here, gelatin functionalized with desaminotyrosine (DAT) or desaminotyrosyl tyrosine (DATT) side chains is crosslinked with cyclodextrin (CD) dimers under formation of inclusions complexes. The supramolecular networks displayed at room temperature decreased water uptake (200-600 wt% for DAT-based systems, 200 wt% for DATT based systems), and increased storage moduli up to 25.6 kPa determined by rheology compared to DAT(T) gelatin. The gel-sol transition temperature increased from 33 up to 42 °C. The presented system that is completely based on natural building blocks may form the basis for materials that may potentially respond by dissolution or changes of properties to changes in environmental conditions or to the presence of CD guest molecules.

Salt-Induced Shape-Memory Effect in Gelatin-Based Hydrogels.

Hydrophilic biopolymers display a strong tendency for self-organization into stable secondary, tertiary, and quaternary structures in aqueous environments. These structures are sensitive to changes in external conditions, such as temperature, pH or ions/salts, which may lead to molecular and/or macroscopic transitions. Here, we report on biopolymer-based stimuli-sensitive switchable matrices showing a shape-memory function as an output being alternatively switched by two different input signals, such as environmental changes in salt concentration or temperature. This was realized by implementing a shape-memory function in hydrogels based on the coil-to-helix transition of protein chains in gelatin-based networks. The hydrogels exhibited mechanical properties similar to that of soft tissue (storage modulus G' = 1-100 kPa) and high swelling capabilities (Q = 1000-3000 vol %). In these gelatin-based networks, the covalent netpoints defined the permanent shape while after deformation helicalization of the gelatin acted as reversible stimuli-sensitive switches providing additional crosslinks capable of fixing the deformed temporary shape. By using either chaotropic salts to suppress gelatin helicalization or kosmotropic salts to support conformational changes of gelatin toward a helical orientation, these additional crosslinks could be cleaved or formed. In bending experiments, the strain fixity (Rf) and strain recovery ratios (Rr) were determined. While Rf ranged from 65 to 95% and was depending on the network composition, Rr were independent of the hydrogel composition with values about 100%. In addition, Rf and Rr were independent of the type of chaotropic salt that was used in this study, showing equal Rf and Rr values for MgCl2, NaSCN, and Mg(SCN)2.

Amides as Non-polymerizable Catalytic Adjuncts Enable the Ring-Opening Polymerization of Lactide With Ferrous Acetate Under Mild Conditions.

Sn-based catalysts are effective in the ring-opening polymerization (ROP) but are toxic. Fe(OAc)2 used as an alternative catalyst is suitable for the ROP of lactide only at higher temperatures (>170°C), associated with racemization. In the ROP of ester and amide group containing morpholinediones with Fe(OAc)2 to polydepsipeptides at 135°C, ester bonds were selectively opened. Here, it was hypothesized that ROP of lactones is possible with Fe(OAc)2 when amides are present in the reactions mixture as Fe-ligands could increase the solubility and activity of the metal catalytic center. The ROP of lactide in the melt with Fe(OAc)2 is possible at temperatures as low as 105°C, in the presence of N-ethylacetamide or N-methylbenzamide as non-polymerizable catalytic adjuncts (NPCA), with high conversion (up to 99 mol%) and yield (up to 88 mol%). Polydispersities of polylactide decreased with decreasing reaction temperature to ≤ 1.1. NMR as well as polarimetric studies showed that no racemization occurred at reaction temperatures ≤145°C. A kinetic study demonstrated a living chain-growth mechanism. MALDI analysis revealed that no side reactions (e.g., cyclization) occurred, though transesterification took place.

Oligodepsipeptide (nano)carriers: Computational design and analysis of enhanced drug loading.

High drug loads of nanoparticles are essential to efficiently provide a desired dosage in the required timeframe, however, these conditions may not be reached with so far established degradable matrices. Our conceptual approach for increasing the drug load is based on strengthening the affinity between drug and matrix in combination with stabilizing drug-matrix-hybrids through strong intermolecular matrix interactions. Here, a method for designing such complex drug-matrix hybrids is introduced employing computational methods (molecular dynamics and docking) as well as experimental studies (affinity, drug loading and distribution, drug release from films and nanoparticles). As model system, dexamethasone (DXM), relevant for the treatment of inflammatory diseases, in combination with poly[(rac-lactide)-co-glycolide] (PLGA) as standard degradable matrix or oligo[(3-(S)-sec-butyl)morpholine-2,5-dione]diol (OBMD) as matrix with hypothesized stronger interaction with DXM were investigated. Docking studies predicted higher affinity of DXM to OBMD than PLGA and displayed amide bond participation in hydrogen bonding with OBMD. Experimental investigations on films and nanoparticles, i.e. matrices of different shapes and sizes, confirmed this phenomenon as shown e.g. by a ~10 times higher solid state solubility of DXM in OBMD than in PLGA. DXM-loaded particles of ~ 150 nm prepared by nanoprecipitation in aqueous environment had a drug loading (DL) up to 16 times higher when employing OBMD as matrix compared to PLGA carriers due to enhanced drug retention in the OBMD phase. Importantly, drug relase periods were not altered as the release from films and particles was mainly ruled by the diffusion length as well as matrix degradation rather than the matrix type, which can be assigned to water diffusing into the matrix and breaking up of drug-matrix hydrogen bonds. Overall, the presented design and fabrication scheme showed predictive power and might universally enable the screening of drug/matrix interactions particularly to expand the oligodepsipeptide platform technology, e.g. by varying the depsipeptide side chains, for drug carrier and release systems.

Characterization of Tissue Transglutaminase as a Potential Biomarker for Tissue Response toward Biomaterials.

Tissue transglutaminase (TGase 2) is proposed to be important for biomaterial-tissue interactions due to its presence and versatile functions in the extracellular environment. TGase 2 catalyzes the cross-linking of proteins through its Ca2+-dependent acyltransferase activity. Moreover, it enhances the interactions between fibronectin and integrins, which in turn mediates the adhesion, migration, and motility of the cells. TGase 2 is also a key player in the pathogenesis of fibrosis. In this study, we investigated whether TGase 2 is present at the biomaterial-tissue interface and might serve as an informative biomarker for the visualization of tissue response toward gelatin-based biomaterials. Two differently cross-linked hydrogels were used, which were obtained by the reaction of gelatin with lysine diisocyanate ethyl ester. The overall expression of TGase 2 by endothelial cells, macrophages, and granulocytes was partly influenced by contact to the hydrogels or their degradation products, although no clear correlation was evidenced. In contrast, the secretion of TGase 2 differed remarkably between the different cells, indicating that it might be involved in the cellular reaction toward gelatin-based hydrogels. The hydrogels were implanted subcutaneously in immunocompetent, hairless SKH1-Elite mice. Ex vivo immunohistochemical analysis of tissue sections over 112 days revealed enhanced expression of TGase 2 around the hydrogels, in particular at days 14 and 21 post-implantation. The incorporation of fluorescently labeled cadaverine derivatives for the detection of active TGase 2 was in accordance with the results of the expression analysis. The presence of an irreversible inhibitor of TGase 2 led to attenuated incorporation of the cadaverines, which verified the catalytic action of TGase 2. Our in vitro and ex vivo results verified TGase 2 as a potential biomarker for tissue response toward gelatin-based hydrogels. In vivo, no TGase 2 activity was detectable, which is mainly attributed to the unfavorable physicochemical properties of the cadaverine probe used.

Interplay between stiffness and degradation of architectured gelatin hydrogels leads to differential modulation of chondrogenesis in vitro and in vivo.

The limited capacity of cartilage to heal large lesions through endogenous mechanisms has led to extensive effort to develop materials to facilitate chondrogenesis. Although physical-chemical properties of biomaterials have been shown to impact in vitro chondrogenesis, whether these findings are translatable in vivo is subject of debate. Herein, architectured 3D hydrogel scaffolds (ArcGel) (produced by crosslinking gelatin with ethyl lysine diisocyanate (LDI)) were used as a model system to investigate the interplay between scaffold mechanical properties and degradation on matrix deposition by human articular chondrocytes (HAC) from healthy donors in vitro and in vivo. Using ArcGel scaffolds of different tensile and shear modulus, and degradation behavior; in this study, we compared the fate of ex vivo engineered ArcGels-chondrocytes constructs, i.e. the traditional tissue engineering approach, with thede novoformation of cartilaginous tissue in HAC laden ArcGels in an ectopic nude mouse model. While the softer and fast degrading ArcGel (LNCO3) was more efficient at promoting chondrogenic differentiation in vitro, upon ectopic implantation, the stiffer and slow degrading ArcGel (LNCO8) was superior in maintaining chondrogenic phenotype in HAC and retention of cartilaginous matrix. Furthermore, surprisingly the de novo formation of cartilage tissue was promoted only in LNCO8. Since HAC cultured for only three days in the LNCO8 environment showed upregulation of hypoxia-associated genes, this suggests a potential role for hypoxia in the observed in vivo outcomes. In summary, this study sheds light on how immediate environment (in vivo versus in vitro) can significantly impact the outcomes of cell-laden biomaterials. STATEMENT OF SIGNIFICANCE: In this study, 3D architectured hydrogels (ArcGels) with different mechanical and biodegradation properties were investigated for their potential to promote formation of cartilaginous matrix by human articular chondrocytes in vitro and in vivo. Two paradigms were explored (i) ex vivo engineering followed by in vivo implantation in ectopic site of nude mice and (ii) short in vitro culture (3 days) followed by implantation to induce de novo cartilage formation. Softer and fast degrading ArcGel were better at promoting chondrogenesis in vitro, while stiffer and slow degrading ArcGel were strikingly superior in both maintaining chondrogenesis in vivo and inducing de novo formation of cartilage. Our findings highlight the importance of the interplay between scaffold mechanics and degradation in chondrogenesis.

Polydepsipeptide Block-Stabilized Polyplexes for Efficient Transfection of Primary Human Cells.

The rational design of a polyplex gene carrier aims to balance maximal effectiveness of nucleic acid transfection into cells with minimal adverse effects. Depsipeptide blocks with an Mn ∼ 5 kDa exhibiting strong physical interactions were conjugated with PEI moieties (2.5 or 10 kDa) to di- and triblock copolymers. Upon nanoparticle formation and complexation with DNA, the resulting polyplexes (sizes typically 60-150 nm) showed remarkable stability compared to PEI-only or lipoplex and facilitated efficient gene delivery. Intracellular trafficking was visualized by observing fluorescence-labeled pDNA and highlighted the effective cytoplasmic uptake of polyplexes and release of DNA to the perinuclear space. Specifically, a triblock copolymer with a middle depsipeptide block and two 10 kDa PEI swallowtail structures mediated the highest levels of transgenic VEGF secretion in mesenchymal stem cells with low cytotoxicity. These nanocarriers form the basis for a delivery platform technology, especially for gene transfer to primary human cells.

Engineering of cell-laden gelatin-based microgels for cell delivery and immobilization in regenerative therapies.

Cell-based therapies often face the challenge of low cell retention and viability upon transplantation. Hence, biomaterials, which can immobilize transplanted cells, while at the same time support cell viability, are essential for successful clinical application. Noteworthy, biomaterials in the micrometer range such as microcapsules or microspheres have the advantage of a minimally invasive introduction into tissue.Hence, we established an approach to generate gelatin-based cell carriers in the form of microspherical hydrogels. Fibroblasts were microencapsulated in glycidylmethacrylate (GMA)-functionalized gelatin by photopolymerization. While the degree of GMA-functionalization was kept constant, the hydrogel cross-linking density was adjusted by varying the time of irradiation or the average gelatin-chain length.Stable microspheres were synthesized from 10 wt% GMA-gelatin solutions for all irradiation periods tested (0.5 -2 min). Evaluation of cell viability revealed that microgels with the same weight content of biopolymer but with decreased cross-linking densities and thus decreased storage and E modulus, resulted in best cell support. Noteworthy, encapsulated cells partially migrated out of the microspheres and attached to the spherical surface.10 wt% GMA-gelatin-based hydrogels with E moduli comparable to the native cellular niche proved to be a promising biomaterial suitable for the production of cell-laden microspheres and shall be evaluated further for biomedical application.

Adipogenic differentiation of human adipose derived mesenchymal stem cells in 3D architectured gelatin based hydrogels (ArcGel).

Polymeric matrices mimicking multiple functions of the ECM are expected to enable a material induced regeneration of tissues. Here, we investigated the adipogenic differentiation of human adipose derived mesenchymal stem cells (hADSCs) in a 3D architectured gelatin based hydrogel (ArcGel) prepared from gelatin and L-lysine diisocyanate ethyl ester (LDI) in an one-step process, in which the formation of an open porous morphology and the chemical network formation were integrated. The ArcGel was designed to support adipose tissue regeneration with its 3D porous structure, high cell biocompatibility, and mechanical properties compatible with human subcutaneous adipose tissue. The ArcGel could support initial cell adhesion and survival of hADSCs. Under static culture condition, the cells could migrate into the inner part of the scaffold with a depth of 840±120 µm after 4 days, and distributed in the whole scaffold (2 mm in thickness) within 14 days. The cells proliferated in the scaffold and the fold increase of cell number after 7 days of culture was 2.55±0.08. The apoptotic rate of hADSCs in the scaffold was similar to that of cells maintained on tissue culture plates. When cultured in adipogenic induction medium, the hADSCs in the scaffold differentiated into adipocytes with a high efficiency (93±1%). Conclusively, this gelatin based 3D scaffold presented high cell compatibility for hADSC cultivation and differentiation, which could serve as a potential implant material in clinical applications for adipose tissue reparation and regeneration.

Poly[acrylonitrile-co-(N-vinyl pyrrolidone)] nanoparticles - Composition-dependent skin penetration enhancement of a dye probe and biocompatibility.

Nanoparticles can improve topical drug delivery: size, surface properties and flexibility of polymer nanoparticles are defining its interaction with the skin. Only few studies have explored skin penetration for one series of structurally related polymer particles with systematic alteration of material composition. Here, a series of rigid poly[acrylonitrile-co-(N-vinyl pyrrolidone)] model nanoparticles stably loaded with Nile Red or Rhodamin B, respectively, was comprehensively studied for biocompatibility and functionality. Surface properties were altered by varying the molar content of hydrophilic NVP from 0 to 24.1% and particle size ranged from 35 to 244nm. Whereas irritancy and genotoxicity were not revealed, lipophilic and hydrophilic nanoparticles taken up by keratinocytes affected cell viability. Skin absorption of the particles into viable skin ex vivo was studied using Nile Red as fluorescent probe. Whilst an intact stratum corneum efficiently prevented penetration, almost complete removal of the horny layer allowed nanoparticles of smaller size and hydrophilic particles to penetrate into viable epidermis and dermis. Hence, systematic variations of nanoparticle properties allows gaining insights into critical criteria for biocompatibility and functionality of novel nanocarriers for topical drug delivery and risks associated with environmental exposure.