Rolling dopant and strain in Y-doped BiFeO3 epitaxial thin films for photoelectrochemical water splitting.

We report significant photoelectrochemical activity of Y-doped BiFeO3 (Y-BFO) epitaxial thin films deposited on Nb:SrTiO3 substrates. The Y-BFO photoanodes exhibit a strong dependence of the photocurrent values on the thickness of the films, and implicitly on the induced epitaxial strain. The peculiar crystalline structure of the Y-BFO thin films and the structural changes after the PEC experiments have been revealed by high resolution X-ray diffraction and transmission electron microscopy investigations. The crystalline coherence breaking due to the small ionic radius Y-addition was analyzed using Willliamson-Hall approach on the 2θ-ω scans of the symmetric (00 l) reflections and confirmed by high resolution TEM (HR-TEM) analysis. In the thinnest sample the lateral coherence length (L∥) is preserved on larger nanoregions/nanodomains. For higher thickness values L∥ is decreasing while domains tilt angles (αtilt) is increasing. The photocurrent value obtained for the thinnest sample was as high as Jph = 0.72 mA/cm2, at 1.4 V(vs. RHE). The potentiostatic scans of the Y-BFO photoanodes show the stability of photoresponse, irrespective of the film's thickness. There is no clear cathodic photocurrent observation for the Y-BFO thin films confirming the n-type semiconductor behavior of the Y-BFO photoelectrodes.

Hysteretic Characteristics of Pulsed Laser Deposited 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3/ZnO Bilayers.

In the present work, we study the hysteretic behavior in the electric-field-dependent capacitance and the current characteristics of 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 (BCZT)/ZnO bilayers deposited on 0.7 wt % Nb-doped (001)-SrTiO3 (Nb:STO) substrates in a metal-ferroelectric-semiconductor (MFS) configuration. The X-ray diffraction measurements show that the BCZT and ZnO layers are highly oriented along the c-axis and have a single perovskite and wurtzite phases, respectively, whereas high-resolution transmission electron microscopy revealed very sharp Nb:STO/BCZT/ZnO interfaces. The capacitance-electric field ( C- E) characteristics of the bilayers exhibit a memory window of 47 kV/cm and a capacitance decrease of 22%, at a negative bias. The later result is explained by the formation of a depletion region in the ZnO layer. Moreover, an unusual resistive switching (RS) behavior is observed in the BCZT films, where the RS ratio can be 500 times enhanced in the BCZT/ZnO bilayers. The RS enhancement can be understood by the barrier potential profile modulation at the depletion region, in the BCZT/ZnO junction, via ferroelectric polarization switching of the BCZT layer. This work builds a bridge between the hysteretic behavior observed either in the C- E and current-electric field characteristics on a MFS structure.

Joining Chemical Pressure and Epitaxial Strain to Yield Y-doped BiFeO3 Thin Films with High Dielectric Response.

BiFeO3 is one of the most promising multiferroic materials but undergoes two major drawbacks: low dielectric susceptibility and high dielectric loss. Here we report high in-plane dielectric permittivity (ε' ∼2500) and low dielectric loss (tan δ < 0.01) obtained on Bi0.95Y0.05FeO3 films epitaxially grown on SrTiO3 (001) by pulsed laser deposition. High resolution transmission electron microscopy and geometric phase analysis evidenced nanostripe domains with alternating compressive/tensile strain and slight lattice rotations. Nanoscale mixed phase/domain ensembles are commonly found in different complex materials with giant dielectric/electromechanical (ferroelectric/ relaxors) or magnetoresistance (manganites) response. Our work brings insight into the joined role of chemical pressure and epitaxial strain on the appearance of nanoscale stripe structure which creates conditions for easy reorientation and high dielectric response, and could be of more general relevance for the field of materials science where engineered materials with huge response to external stimuli are a highly priced target.

Functionalized magnetite silica thin films fabricated by MAPLE with antibiofilm properties.

We report on the fabrication of magnetite/salicylic acid/silica shell/antibiotics (Fe(3)O(4)/SA/SiO(2)/ATB) thin films by matrix-assisted pulsed laser evaporation (MAPLE) to inert substrates. Fe(3)O(4)-based powder have been synthesized and investigated by XRD and TEM. All thin films were studied by FTIR, SEM and in vitro biological assays using Staphylococcus aureus and Pseudomonas aeruginosa reference strains, as well as eukaryotic HEp-2 cells. The influence of the obtained nanosystems on the microbial biofilm development as well as their biocompatibility has been assessed. For optimum deposition conditions, we obtained uniform adherent films with the composition identical with the raw materials. Fe(3)O(4)/SA/SiO(2)/ATB thin films had an inhibitory activity on the ability of microbial strains to initiate and develop mature biofilms, in a strain- and antibiotic-dependent manner. These magnetite silica thin films are promising candidates for the development of novel materials designed for the inhibition of medical biofilms formed by different pathogenic agents on common substrates, frequently implicated in the etiology of chronic and hard to treat infections.