Negatively Charged Porous Thin Film from ABA Triblock Copolymer Assembly.

The preparation of well-arranged nano-porous thin films from an ABA triblock copolymer of polystyrene-block-poly(sodium 4-styrenesulfonate)-block-polystyrene (PS-PNaSS-PS) is reported. This copolymer was self-assembled in a N,N-dimethylformamide (DMF)/water mixture and the resulting micellar solution was used to prepare thin films via the compact packing of the flower-like micelles using spin coating method. The films were characterized by several microscopy techniques such as TEM, AFM, and SEM. Permeation test was performed to highlight the interconnected porous nature of the polymeric network obtained. Under applied water pressure, the micellar morphology was altered and a partial fusion of the micelles was observed that resulted in a change in the water permeability. Such hydrophilic nanoporous thin films with negatively charged interface could find applications in membrane filtration.

Translocation across a self-healing block copolymer membrane.

Herein, a membrane prepared from the self-assembly of poly(styrene-co-acrylonitrile)-b-poly(ethylene oxide)-b-poly(styrene-co-acrylonitrile) micelles is found to exhibit translocation of nano-objects dispersed in aqueous solution. With the water flow as a driving force, temporary pores are created in between the micelles to facilitate the passage of nano-objects. These temporary pores close afterwards through a self-healing mechanism. As main results, polystyrene and silica nanoparticles exhibited a selective translocation directly influenced by their size and applied pressure.

Anti-Bioadhesive Coating Based on Easy to Make Pseudozwitterionic RAFT Block Copolymers for Blood-Contacting Applications.

Amphiphilic diblock copolymer containing randomly distributed positive and negative charged monomers are synthesized using RAFT polymerization technique to be used as anti-bioadhesion coatings for hydrophobic surfaces. Quaternized 2-(dimethylamino) ethyl methacrylate and potassium 3-sulfopropyl methacrylate (P[qDMAEMA-co-KSPMA]) are randomly polymerized to yield an anti-bioadhesion block which is, in one pot, copolymerized with styrene as an anchoring block. This copolymer has demonstrated high anti-bioadhesion properties to avoid the blood clotting in medical devices through a simple and facile approach to preparation of pseudozwitterionic copolymers.