Tailoring Nanoscale Morphology of Polymer:Fullerene Blends Using Electrostatic Field.

To tailor the nanomorphology in polymer/fullerene blends, we study the effect of electrostatic field (E-field) on the solidification of poly(3-hexylthiophene-2, 5-diyl) (P3HT):[6,6]-phenyl-C61-butyric acid methyl ester (PC60BM) bulk heterojunction (BHJ). In addition to control; wet P3HT:PC60BM thin films were exposed to E-field of Van de Graaff (VDG) generator at three different directions-horizontal (H), tilted (T), and vertical (V)-relative to the plane of the substrate. Surface and bulk characterizations of the field-treated BHJs affirmed that fullerene molecules can easily penetrate the spaghetti-like P3HT and move up and down following the E-field. Using E-field treatment, we achieved favorable morphologies with efficient charge separation, transport, and collection. We improve; (1) the hole mobility values up to 19.4 × 10-4 ± 1.6 × 10-4 cm2 V-1 s-1 and (2) the power conversion efficiency (PCE) of conventional and inverted OPVs up to 2.58 ± 0.02% and 4.1 ± 0.40%, respectively. This E-field approach can serve as a new morphology-tuning technique, which is generally applicable to other polymer-fullerene systems.

Versatile Role of Solvent Additive for Tailoring Morphology in Polymer Solar Cells for Efficient Charge Transport.

In this work role of solvent additive namely 1,8 diiodoctane (DIO) on the nanoscale morphology and its relation with the charge transport of poly(diketopyrrolopyrrole-terthiophene) (PDPP3T):PCBM solar cells has been investigated. Addition of DIO led to enhanced structural ordering as observed from optical measurements. Photovoltaic devices processed with DIO additive showed improved efficiencies due to significant enhancement in short circuit current density. Atomic force microscopy (AFM) and Kelvin probe force microscopy (KPFM) images showed that DIO led to finer phase segregation that gave rise to better photovoltaic performance in additive processed active layers. Photoinduced current extraction by linearly increasing voltage (P-CELIV) measurements on PDPP3T:PCBM solar cells revealed higher mobility and extracted charge carrier density for DIO processed devices.

Enhanced Lifetime of Polymer Solar Cells by Surface Passivation of Metal Oxide Buffer Layers.

The role of electron selective interfaces on the performance and lifetime of polymer solar cells were compared and analyzed. Bilayer interfaces consisting of metal oxide films with cationic polymer modification namely poly ethylenimine ethoxylated (PEIE) were found to enhance device lifetime compared to bare metal oxide films when used as an electron selective cathode interface. Devices utilizing surface-modified metal oxide layers showed enhanced lifetimes, retaining up to 85% of their original efficiency when stored in ambient atmosphere for 180 days without any encapsulation. The work function and surface potential of zinc oxide (ZnO) and ZnO/PEIE interlayers were evaluated using Kelvin probe and Kelvin probe force microscopy (KPFM) respectively. Kelvin probe measurements showed a smaller reduction in work function of ZnO/PEIE films compared to bare ZnO films when aged in atmospheric conditions. KPFM measurements showed that the surface potential of the ZnO surface drastically reduces when stored in ambient air for 7 days because of surface oxidation. Surface oxidation of the interface led to a substantial decrease in the performance in aged devices. The enhancement in the lifetime of devices with a bilayer interface was correlated to the suppressed surface oxidation of the metal oxide layers. The PEIE passivated surface retained a lower Fermi level when aged, which led to lower trap-assisted recombination at the polymer-cathode interface. Further photocharge extraction by linearly increasing voltage (Photo-CELIV) measurements were performed on fresh and aged samples to evaluate the field required to extract maximum charges. Fresh devices with a bare ZnO cathode interlayer required a lower field than devices with ZnO/PEIE cathode interface. However, aged devices with ZnO required a much higher field to extract charges while aged devices with ZnO/PEIE showed a minor increase compared to the fresh devices. Results indicate that surface modification can act as a suitable passivation layer to suppress oxidation in metal oxide thin films for enhanced lifetime in inverted organic solar cells.

Benzothiadiazole-based polymer for single and double junction solar cells with high open circuit voltage.

Single and double junction solar cells with high open circuit voltage were fabricated using poly{thiophene-2,5-diyl-alt-[5,6-bis(dodecyloxy)benzo[c][1,2,5]thiadiazole]-4,7-diyl} (PBT-T1) blended with fullerene derivatives in different weight ratios. The role of fullerene loading on structural and morphological changes was investigated using atomic force microscopy (AFM) and X-ray diffraction (XRD). The XRD and AFM measurements showed that a higher fullerene mixing ratio led to breaking of inter-chain packing and hence resulted in smaller disordered polymer domains. When the PBT-T1:PC60BM weight ratio was 1 : 1, the polymer retained its structural order; however, large aggregated domains formed, leading to poor device performance due to low fill factor and short circuit current density. When the ratio was increased to 1 : 2 and then 1 : 3, smaller amorphous domains were observed, which improved photovoltaic performance. The 1 : 2 blending ratio was optimal due to adequate charge transport pathways giving rise to moderate short circuit current density and fill factor. Adding 1,8-diiodooctane (DIO) additive into the 1 : 2 blend films further improved both the short circuit current density and fill factor, leading to an increased efficiency to 4.5% with PC60BM and 5.65% with PC70BM. These single junction solar cells exhibited a high open circuit voltage at ∼ 0.9 V. Photo-charge extraction by linearly increasing voltage (Photo-CELIV) measurements showed the highest charge carrier mobility in the 1 : 2 film among the three ratios, which was further enhanced by introducing the DIO. The Photo-CELIV measurements with varying delay times showed significantly higher extracted charge carrier density for cells processed with DIO. Tandem devices using P3HT:IC60BA as bottom cell and PBT-T1:PC60BM as top cell exhibited a high open circuit voltage of 1.62 V with 5.2% power conversion efficiency.

Interplay of nanoscale domain purity and size on charge transport and recombination dynamics in polymer solar cells.

Charge transport and bimolecular recombination dynamics were correlated with nanomorphology in polymer solar cells. The morphology of poly(diketopyrrolopyrrole-terthiophene) (PDPP3T) and phenyl-C61-butyric acid methyl ester (PC60BM) blend films was modified using different solvent additives namely 1-chloronaphthalene (CN), 1,8-diiodooctane (DIO) and 1,8-octanedithiol (ODT) and their role on steady state and transient optoelectronic properties was investigated. The energy filtered transmission electron microscopy (EFTEM) images showed that additives (e.g. CN and DIO) improved the domain purity which leads to significantly higher short circuit current densities (Jsc). However when the cells were processed with the ODT additive, the fill factor (FF) and open circuit voltage (Voc) decreased dramatically. Films processed with the ODT additive showed a smaller domain size but were more connected compared to films processed using CN and DIO additives. Transient photocurrent analysis indicates faster charge collection in the case of CN and DIO processed solar cells and the slowest charge collection in ODT processed solar cells. Interestingly devices processed with the ODT additive also showed the longest charge carrier recombination lifetime and lowest bimolecular recombination coefficient. This is attributed to the smaller donor domains that are connected with each other to provide a more interconnected and efficient charge transport matrix but longer pathways in ODT films. Such a matrix helped the charge to escape from the donor-acceptor interfaces and thus reduces the bimolecular recombination, while the longer pathway increases the charge collection time. Further insight is provided into the selection of processing conditions to achieve an ideal active layer morphology consisting of domains with higher polymer purity and optimal size that lead to higher Jsc and FF.