Temperature dependence of the dielectric function and critical points of α-SnS from 27 to 350 K.

We report the temperature dependence of the dielectric function ε = ε1 + iε2 and critical point (CP) energies of biaxial α-SnS in the spectral energy region from 0.74 to 6.42 eV and temperatures from 27 to 350 K using spectroscopic ellipsometry. Bulk SnS was grown by temperature gradient method. Dielectric response functions were obtained using multilayer calculations to remove artifacts due to surface roughness. We observe sharpening and blue-shifting of CPs with decreasing temperature. A strong exciton effect is detected only in the armchair direction at low temperature. New CPs are observed at low temperature that cannot be detected at room temperature. The temperature dependences of the CP energies were determined by fitting the data to the phenomenological expression that contains the Bose-Einstein statistical factor and the temperature coefficient for describing the electron-phonon interaction.

Optical phonons of SnSe(1-x)Sx layered semiconductor alloys.

The evolution of the optical phonons in layered semiconductor alloys SnSe(1-x)Sx is studied as a function of the composition by using polarized Raman spectroscopy with six different excitation wavelengths (784.8, 632.8, 532, 514.5, 488, and 441.6 nm). The polarization dependences of the phonon modes are compared with transmission electron diffraction measurements to determine the crystallographic orientation of the samples. Some of the Raman modes show significant variation in their polarization behavior depending on the excitation wavelengths. It is established that the maximum intensity direction of the Ag2 mode of SnSe(1-x)Sx (0 ≤ x ≤ 1) does not depend on the excitation wavelength and corresponds to the armchair direction. It is additionally found that the lower-frequency Raman modes of Ag1, Ag2 and B3g1 in the alloys show the typical one-mode behavior of optical phonons, whereas the higher-frequency modes of B3g2, Ag3 and Ag4 show two-mode behavior.