ABSTRACT
The interaction between the intrinsic polarity of the host material and the TADF guest material affects charge injection and transport, exciton formation, charge recombination, and emission mechanisms. Therefore, understanding and controlling the interaction between the intrinsic polarity of the host material and the TADF guest material is very important to realize efficient TADF-OLED devices. This study investigated the molecular interaction between different polar host materials and a thermally activated delayed fluorescence material (DMAc-PPM). It has been found that interaction between the host and guest (π-π stacking interaction, multiple CH/π contacts) greatly influence the molecular transition dipole moment orientation of the guest. And the OLED devices based on the strong polar host (DPEPO) exhibited the highest EQEmax and lowest luminescence intensity, while devices using the weaker polar hosts mCP and CBP achieved higher luminance and lower EQEmax. Then, the strong polar host DPEPO was mixed with the weaker polar hosts CBP and mCP, respectively. The devices prepared based on the mixed-host DPEPO: mCP showed a 2.2 times improvement in EQEmax from 6.3% to 20.1% compared to the single-host mCP. The devices prepared based on the mixed-host DPEPO: CBP showed a 3.1 times improvement in luminance intensity from 1023 cd/m2 to 4236 cd/m2 compared to the single host of DPEPO. This suggests that optimizing the polarity of host materials has the potential to enhance the performance of solution prepared OLED devices.