Influence of Phosphate on Network Connectivity and Glass Transition in Highly Polymerized Aluminosilicate Glasses.

Melt-derived metaluminous (Al/Na = 1) aluminosilicate glasses in the system SiO2-Al2O3-Na2O-P2O5 were prepared with P2O5 and SiO2 contents varying from 0 to 7.5 and 50 to 70 mol %, respectively. The glass structure was investigated by X-ray absorption near edge structure, far- and medium-infrared, and polarized Raman spectroscopic techniques. The results indicate the incorporation of phosphate into the aluminosilicate network not only as partially depolymerized groups but also as fully polymerized groups charge-balanced by aluminate units in Al-O-P bonds. A new analysis method based on polarized Raman spectra in the bending frequency range indicates a preference of phosphate to reorganize the smallest ring structures. Changes in the glass transition temperature with the increase in phosphate content were found to be consistent with the depolymerization of the network structure shown by spectroscopy. By contrast, increasing the silica content by substituting SiO4 for AlO4 tetrahedra, while keeping the phosphate content constant, was found to have a negligible effect on network polymerization. Still, the glass transition temperature decreased and correlated with a far-infrared sodium band shift to higher frequency. This was interpreted as local changes in bond strength caused by complex interactions between the different network formers and sodium ions.

Structural Role of Phosphate in Metaluminous Sodium Aluminosilicate Glasses As Studied by Solid State NMR Spectroscopy.

In this contribution we present a detailed study of the effect of the addition of small to intermediate amounts of P2O5 (up to 7.5 mol %) on the network organization of metaluminous sodium aluminosilicate glasses employing a range of advanced solid state NMR methodologies. The combined results from MAS, MQMAS (multiple quantum MAS), or MAT (magic angle turning) NMR spectroscopy and a variety of dipolar based NMR experiments-27Al{31P}-, 27Al{29Si}-, 29Si{31P}-, and 31P{29Si}-REDOR (rotational echo double resonance) NMR spectroscopy as well as 31P{27Al}- and 29Si{27Al}-REAPDOR (rotational echo adiabatic passage double resonance) NMR-allow for a detailed analysis of the network organization adopted by these glasses. Phosphate is found as QP2, QP3, and QP4 (with the superscript denoting the number of bridging oxygens), the QP4 units can be safely identified with the help of 31P MAT NMR experiments. Al exclusively adopts a 4-fold coordination. The withdrawal of a fraction of the sodium cations from AlO4 units that is needed for charge compensation of the QP2 units necessitates an alternative charge compensation scheme for these AlO4 units via formation of QP4 units or oxygen triclusters. The dipolar NMR experiments suggest a strong preference of P for Al with an average value of ca. 2.4 P-O-Al connections per phosphate tetrahedron. P is thus mainly integrated into the network via P-O-Al bonding, the formation of Si-O-P bonding plays only a minor role.