ABSTRACT
The conductor aluminum alloys of Al-0.25wt.%Zr alloyed additionally with X = Er, Si, Hf and Nb were the objects of our investigations. The fine-grained microstructure in the alloys was formed via equal channel angular pressing and rotary swaging. The thermal stability of the microstructure, specific electrical resistivity and microhardness of the novel conductor aluminum alloys were investigated. The mechanisms of nucleation of the Al3(Zr, X) secondary particles during annealing the fine-grained aluminum alloys were determined using the Jones-Mehl-Avrami-Kolmogorov equation. Using the Zener equation, the dependencies of the average secondary particle sizes on the annealing time were obtained on the base of the analysis of the data on the grain growth in the aluminum alloys. The secondary particle nucleation during long-time low-temperature annealing (300 °C, 1000 h) was shown to go preferentially at the cores of the lattice dislocations. The Al-0.25%Zr-0.25%Er-0.20%Hf-0.15%Si alloy subjected to long-time annealing at 300 °C has the optimal combination of microhardness and electrical conductivity (59.8%IACS, Hv = 480 ± 15 MPa).
ABSTRACT
The article presents the results of the investigation of the mechanism of the densification behavior of alumina-based ceramics during spark plasma sintering. The role of the heating rates and additives were investigated. The first (initial) stage of sintering was investigated by the Young-Cutler model. The second (intermediate) stage of sintering was investigated as a process of plastic deformation of a porous body under external pressure. It was shown that, at the initial stage, the formation of necks between the particles is controlled by grain boundary diffusion (the activation energy is Qb ≈ 20 kTm). At this stage, accommodation of the shape of the alumina particles is also occurring (an increase in the packing density). The accommodation process facilitates the shrinkage of the powder, which is reflected in a decrease in the effective activation energy of shrinkage at low heating rates (10 °C/min) to Qb ≈ 17 kTm. At heating rates exceeding 10 °C/min, the intensity of the processes of accommodation of alumina particles turns out to be much slower than the existing diffusion processes of growth of necks between the alumina particles. It was shown that the grain boundary sliding mechanism that occurs in the second stage of sintering can play a decisive role under conditions of spark plasma sintering with a high heating rate. The found value of the activation energy at the second stage of sintering is also close to the activation energy of grain-boundary diffusion of alumina (Qb ≈ 20 kTm). The influences of the second phase particles of MgO, TiO2, and ZrO2 on densification behavior of alumina-based ceramics were investigated. Since at the first stage of sintering the densification relates with the formation of necks between the particles of alumina, the additives (0.5% vol) have no noticeable effect on this process. It was also shown that the second phase particles which are located at the grain boundaries of alumina are not involved in the slip process during the second sintering stage. Analysis shows that additives act only in the final (third) stage of spark plasma sintering of alumina.