ABSTRACT
The results of a detailed study of magnetic properties and of the microstructure of SiMn films with a small deviation from stoichiometry are presented. The aim was to reveal the origin of the high temperature ferromagnetic ordering in such compounds. Unlike SiMn single crystals with the Curie temperature ~30 K, considered Si1-x Mn x compounds with x = 0.5 +Δx and Δx in the range of 0.01-0.02 demonstrate a ferromagnetic state above room temperature. Such a ferromagnetic state can be explained by the existence of highly defective B20 SiMn nanocrystallites. These defects are Si vacancies, which are suggested to possess magnetic moments. The nanocrystallites interact with each other through paramagnons (magnetic fluctuations) inside a weakly magnetic manganese silicide matrix giving rise to a long range ferromagnetic percolation cluster. The studied structures with a higher value of Δx ≈ 0.05 contained three different magnetic phases: (a)-the low temperature ferromagnetic phase related to SiMn; (b)-the above mentioned high temperature phase with Curie temperature in the range of 200-300 K depending on the growth history and
ABSTRACT
The technique of laser-induced atomic-ionization (AI) in flames has been used for direct determination of Na, K, Rb, and Cs in samples such as water, high-purity alkali metals and their salts and polymeric organosilicon compounds. Different procedures for sample introduction into the flame were studied: (a) the sample was placed onto the cathode of the detector (this gave limits of detection for Na and Cs of 4 x 10(-16) and 2 x 10(-15) g, respectively), (b) electrothermal vaporization and (c) aspiration of the sample into the flame. To reduce the interference of SiO(2) in the AI determination of K in polymeric organosilicon compounds (at the level of 10(-3)-10(-5)%), a procedure involved additional electrical heating of the FID cathode was developed. The efficiency of certain schemes for the laser stepwise and two-photon excitation of atoms was compared for determination of Na.