ABSTRACT
The persistent issue of ceramic membrane fouling poses significant challenges to its widespread implementation. To address this concern, ozone nanobubbles (ozone-NBs) have garnered attention due to their remarkable mass transfer efficiency. In this investigation, we present a novel ozone-NB generator system to effectively clean a fouled ceramic membrane that is typically employed in the dye industry. The surface characteristics of the ceramic membrane underwent significant alterations, manifesting incremental changes in surface roughness and foulant accumulation reduction, as evidenced in atomic force microscopy, scanning electron microscopy, X-ray fluorescence, and energy-dispersive spectroscopy. Remarkably, the sequential 4 h cleaning process demonstrates an effective outcome leading to an almost 2-fold enhancement in the membrane flux. The initial fouled state of 608 L/h/m2 increased to 1050 L/h/m2 in the 4 h state with a recovery of 50%. We propose such membrane performance improvement governed by the ozone-NBs with a size distribution of 213.2 nm and a zeta potential value of -20.26 ± 0.13 mV, respectively. This effort showcases a substantial innovative and sustainable technology approach toward proficient foulant removal in water treatment applications.
ABSTRACT
The electrospun nanofiber membrane from polyvinyl chloride (PVC) waste for water treatment applications has been successfully produced. The PVC precursor solution was prepared by dissolving the PVC waste in DMAc solvent, and a centrifuge was used to separate undissolved materials from the precursor solution. Ag and TiO2 were added to the precursor solution before the electrospinning process. We studied the fabricated PVC membranes using SEM, EDS, XRF, XRD, and FTIR to study the fiber and membrane properties. The SEM images depicted that Ag and TiO2 addition has changed the morphology and size of fibers. The EDS images and XRF spectra confirmed the presence of Ag and TiO2 on the nanofiber membrane. The XRD spectra showed the amorphous structure of all membranes. The FTIR result indicated that the solvent completely evaporated throughout the spinning process. The fabricated PVC@Ag/TiO2 nanofiber membrane showed the photocatalytic degradation of dyes under visible light. The filtration test on the membrane PVC and PVC@Ag/TiO2 depicted that the presence of Ag and TiO2 affected the flux and separation factor of the membrane.
ABSTRACT
Nanofiber membranes were successfully synthesized from expanded polystyrene (EPS) waste with the addition of poly(vinylpyrrolidone) (PVP) for water microfiltration using the electrospinning method. The EPS-based nanofiber membranes exhibited a smooth morphology and were uniform in size. The concentration of the EPS/PVP solution changed some of the physical parameters of the nanofiber membrane, such as viscosity, conductivity, and surface tension. Greater viscosity and surface tension increase the nanofiber membrane diameter, whereas the addition of PVP results in hydrophilicity. Additionally, increasing the pressure increased the flux value of each variation of the nanofiber membranes. Furthermore, the rejection value was 99.99% for all variations. Finally, the use of EPS waste for nanofiber membranes is also beneficial for decreasing the amount of EPS waste in the environment and is an alternative to the current membranes available in the market for water filtration applications.
ABSTRACT
Acrylonitrile butadiene styrene (ABS) is one of the most common fused-filament feedstocks for 3D printing. The rapid growth of the 3D printing industry has resulted in huge demand for ABS filaments; however, it generates a large amount of waste. This study developed a novel method using waste ABS to fabricate electrospun nanofiber membranes (ENMs) for water filtration. Polyvinylpyrrolidone (PVP) was employed to modify the properties of waste ABS, and the effect of PVP addition in the range of 0-5 wt% was investigated. The results showed that adding PVP increased the viscosity and surface tension but decreased the conductivity of the precursor solution. After electrospinning, PVP could reduce the number of beads, increase the porosity and fiber diameter, and improve the wettability of the fabricated fibers. Moreover, the bilayer of ABS ENMs achieved a high flux value between 2951 and 48 041 L m-2 h-1 and a high rejection rate of 99%. Our study demonstrates a sustainable strategy to convert waste plastics to inexpensive materials for wastewater treatment membranes.