Rapid lipid bilayer membrane formation on Parylene coated apertures to perform ion channel analyses.

We present a chip design allowing rapid and robust lipid bilayer (LBL) membrane formation using a Parylene coated thin silicon nitride aperture. After bilayer formation, single membrane channels can be reconstituted and characterized by electrophysiology. The ability for robust reconstitution will allow parallelization and enhanced screening of small molecule drugs acting on or permeating across the membrane channel. The aperture was realized on a microfabricated silicon nitride membrane by using standard clean-room fabrication processes. To ensure the lipid bilayer formation, the nitride membrane was coated with a hydrophobic and biocompatible Parylene layer. We tested both Parylene-C and Parylene-AF4. The contact angle measurements on both Parylene types showed very good hydrophobic properties and affinity to lipids. No precoating of the Parylene with an organic solvent is needed to make the aperture lipophilic, in contradiction to Teflon membranes. The chips can be easily placed in an array utilizing a 3D printed platform. Experiments show repetitive LBL formation and destruction (more than 6 times) within a very short time (few seconds). Through measurements we have established that the LBL layers are very thin. This allows the investigation of the fusion process of membrane proteins i.e. outer membrane protein (OmpF) in the LBL within a few minutes.

Ultrahigh-mobility graphene devices from chemical vapor deposition on reusable copper.

Graphene research has prospered impressively in the past few years, and promising applications such as high-frequency transistors, magnetic field sensors, and flexible optoelectronics are just waiting for a scalable and cost-efficient fabrication technology to produce high-mobility graphene. Although significant progress has been made in chemical vapor deposition (CVD) and epitaxial growth of graphene, the carrier mobility obtained with these techniques is still significantly lower than what is achieved using exfoliated graphene. We show that the quality of CVD-grown graphene depends critically on the used transfer process, and we report on an advanced transfer technique that allows both reusing the copper substrate of the CVD growth and making devices with mobilities as high as 350,000 cm(2) V(-1) s(-1), thus rivaling exfoliated graphene.