ABSTRACT
The carbonophosphate Na3FePO4CO3 was synthesized by the mechanical ball milling method for the first time. The composition of the obtained sample with a higher amount of Fe2+ was Na2.66Fe2+0.66Fe3+0.34PO4CO3 as confirmed by Mössbauer analysis, owing to the good airtight properties of this method. The obtained samples in an organic electrolyte delivered an initial discharge capacity of 124 mAh/g at room temperature, and a larger discharge capacity of 159 mAh/g (1.66 Na+/mole) at 60 °C. With 17 m NaClO4 aqueous electrolyte, a discharge capacity of 161 mAh/g (1.69 Na+/mole) was delivered because of the high ionic conductivity of the concentrated aqueous electrolyte. During the charge-discharge process, the formation of Fe4+ after charging up to 4.5 V and the return of Fe2+ after discharging down to 1.5 V were detected by ex-situ X-ray absorption near edge structure (XANES) analysis.
ABSTRACT
Visible-Light active photocatalytic tungsten trioxide (WO3) films were deposited at a substrate temperature of 800 degrees C by dc reactive magnetron sputtering using a W metal target. In addition, Platinum (Pt) was deposited on the WO3 film surfaces at room temperature, also by sputtering. In the early stages of Pt growth, formation of Pt nanoparticles could be expected because of the island structure observed in Volmer-Weber-type growth mode. The surface coverage of Pt on the WO3 films was estimated quantitatively by X-ray photoelectron spectroscopy and was found to be approximately 60% after 7 s deposition. High resolution electron microscopy (HREM) demonstrated that Pt nanoparticles with a diameter of about 2.5 nm were generated and dispersed uniformly on the entire surface area of the columnar polycrystalline WO3 films. These Pt-loaded films exhibited high photocatalytic activity in the decomposition of acetaldehyde (CH3CHO) under visible light irradiation.