Optimizing Anisotropic Polyurethane Scaffolds to Mechanically Match with Native Myocardium.

Biodegradable cardiac patch is desirable to possess mechanical properties mimicking native myocardium for heart infarction treatment. We fabricated a series of anisotropic and biodegradable polyurethane porous scaffolds via thermally induced phase separation (TIPS) and tailored their mechanical properties by using various polyurethanes with different soft segments and varying polymer concentrations. The uniaxial mechanical properties, suture retention strength, ball-burst strength, and biaxial mechanical properties of the anisotropic porous scaffolds were optimized to mechanically match native myocardium. The optimal anisotropic scaffold had a ball burst strength (20.7 ± 1.5 N) comparable to that of native porcine myocardium (20.4 ± 6.0 N) and showed anisotropic behavior close to biaxial stretching behavior of the native porcine myocardium. Furthermore, the optimized porous scaffold was combined with a porcine myocardium-derived hydrogel to form a biohybrid scaffold. The biohybrid scaffold showed morphologies similar to the decellularized porcine myocardial matrix. This combination did not affect the mechanical properties of the synthetic scaffold alone. After in vivo rat subcutaneous implantation, the biohybrid scaffolds showed minimal immune response and exhibited higher cell penetration than the polyurethane scaffold alone. This biohybrid scaffold with biomimetic mechanics and good tissue compatibility would have great potential to be applied as a biodegradable acellular cardiac patch for myocardial infarction treatment.

Mechanical Strength, Biodegradation, and in Vitro and in Vivo Biocompatibility of Zn Biomaterials.

Zn-based biomaterials have emerged as promising new types of bioresorbable metallics applicable to orthopedic devices, cardiovascular stents, and other medical applications recently. Compared to other degradable metallic biomaterials (i.e., Mg- or Fe-based), Zn biomaterials have a more appropriate corrosion rate without hydrogen gas evolution. Here, we evaluated the potential of Zn-based metallics as medical implants, both in vitro and in vivo, alongside a standard benchmark Mg alloy, AZ31. The mechanical properties of the pure Zn were not strong enough but were significantly enhanced (microhardness > 70 kg/mm2, strength > 220 MPa, elongation > 15%) after alloying with Sr or Mg (1.5 at. %), surpassing the minimal design criteria for load-bearing device applications. The corrosion rate of Zn-based biomaterials was about 0.4 mm/year, significantly slower than that of AZ31. The measured cell viability and proliferation of three different human primary cells fared better for Zn-based biomaterials than AZ31 using both direct and indirect culture methods. Platelet adhesion and activation on Zn-based materials were minimal, significantly less than on AZ31. The hemolysis ratio of red cells (<0.5%) after incubation with Zn-based materials was also well below the ISO standard of 5%. Moreover, Zn-based biomaterials promoted stem cell differentiation to induce the extracellular matrix mineralization process. In addition, in vivo animal testing using subcutaneous, bone, and vascular implantations revealed that the acute toxicity and immune response of Zn-based biomaterials were minimal/moderate, comparable to that of AZ31. No extensive cell death and foreign body reactions were observed. Taken together, Zn-based biomaterials may have a great potential as promising candidates for medical implants.