ABSTRACT
A series of poly(ethylene oxide)/poly(butylene terephthalate) (PEO/PBT) segmented block copolymer films was treated with a radio-frequency carbon dioxide (CO(2)) or with argon (Ar) plasma. The effects of (preferential) etching on surface structure, topography, chemistry, and wettability were studied by scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, and contact angle measurements. In all cases, a granular-type nanostructure was formed after prolonged CO(2) plasma etching. Ar plasma etching generally did not lead to significant changes in surface structure. Regarding surface chemistry, CO(2) plasma treatment caused surface oxidation and oxidative degradation of the films while Ar plasma etching resulted mainly in the preferential removal of PEO blocks. The wettability of all films significantly increased after plasma treatment because of the creation of polar functional groups at the surface. Preliminary goat bone-marrow cell compatibility experiments have shown that all plasma-treated PEO/PBT films induced a greatly enhanced cell adhesion and/or growth compared to untreated biomaterials. This improvement was attributed to changes in surface chemistry during plasma etching rather than to changes in surface structure. These results show that plasma-treated PEO/PBT copolymers have a high potential as scaffolds for bone tissue regeneration.
Subject(s)
Biocompatible Materials/chemistry , Polyesters/chemistry , Polyethylene Glycols/chemistry , Animals , Bone Marrow Cells/cytology , Carbon Dioxide , Cell Adhesion , Cell Division , Goats , Materials Testing , Microscopy, Atomic Force , Microscopy, Electron, Scanning , Spectrum Analysis , Surface Properties , Tissue Engineering , X-RaysABSTRACT
Cellulose triacetate (CTA) ultrafilters and cellulose acetate blend (CAB) desalination membranes were treated with a radiofrequency gas plasma (tetrafluoromethane (CF(4)) or carbon dioxide (CO(2)), 47-49 W, 0.04-0.08 mbar). Treatment times were varied between 15 s and 120 min. The plasma-treated top layer of the membranes was characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, and contact angle measurements to obtain information about surface structure, chemistry, and wettability, respectively. The membrane properties (e.g., permeability, selectivity, fouling) were studied by waterflux measurements, molecular weight cutoff measurements, and fouling experiments with bovine serum albumin. CO(2) plasma treatment resulted in gradual etching of the membrane's dense top layer. Permeation and selectivity changed significantly for treatment times of 0-15 min for CTA and 5-60 min for CAB membranes. Moreover, CTA membranes were hydrophilized during CO(2) plasma treatment whereas CF(4) plasma treatment led to hydrophobic surfaces due to strong fluorination of the top layer. This study shows that gas plasma etching can tailor the properties of asymmetric cellulose acetate membranes by simultaneously modifying the chemistry and structure of the top layer. The low fouling properties of CTA membranes were thereby largely maintained.