ABSTRACT
This work investigates the performance and structure of polyamide thin film nanocomposite (PA-TFN) membrane incorporated with triethylenetetramine-modified graphene oxide (GO-TETA). The embedment of GO-TETA nanosheets within the structure of PA-TFN membrane was evaluated at different concentrations (0.005, 0.01, 0.03 wt%; in aqueous piperazine (PIP)) through interfacial polymerization (IP). The physicochemical properties of the prepared membrane were investigated by SEM, AFM, water contact angle, and zeta potential as well as ATR-IR spectroscopy. The presence of longer chains of amino groups (in comparison with the directly linked amino ones) among the stacked GO nanosheets was assumed to increase interlayer spacing, resulting in remarkable changes in water permeance and separation behavior of modified polyamide (PA) membrane. It is seen that GO-TETA nanosheets were uniformly distributed in the matrix of PA layer. With increasing the concentration of GO-TETA, the flux of TFN membranes under 6 bar was increased from 49.8 l/m2 h (no additive) to 73.2 l/m2 h (TFN comprising 0.03 wt% GO-TETA. In addition, more loading GO-TETA resulted in a significant decrease in the average thickness of the polyamide layer from ~380 to ~150 nm. Furthermore, addition of GO-TETA improved the hydrophilicity of nanocomposite membranes, resulting in superb water flux recovery (antifouling indicator) as high as 95% after filtration of bovine serum albumin solution. Also, the retention capability of the TFN membranes towards some textile dyes increased as high as 99.6%.
Subject(s)
Graphite , Water Purification , Nylons , TrientineABSTRACT
An experimental study of bioethanol adsorption on natural Iranian clinoptilolite was carried out. Dynamic breakthrough curves were used to investigate the best adsorption conditions in bioethanol liquid phase. A laboratory setup was designed and fabricated for this purpose. In order to find the best operating conditions, the effect of liquid pressure, temperature and flow rate on breakthrough curves and consequently, maximum ethanol uptake by adsorbent were studied. The effects of different variables on final bioethanol concentration were investigated using Response Surface Methodology (RSM). The results showed that by working at optimum condition, feed with 96% (v/v) initial ethanol concentration could be purified up to 99.9% (v/v). In addition, the process was modeled using Box-Behnken model and optimum operational conditions to reach 99.9% for final ethanol concentration were found equal to 10.7 °C, 4.9 bar and 8 mL/min for liquid temperature, pressure and flow rate, respectively. Therefore, the selected natural Iranian clinoptilolite was found to be a promising adsorbent material for bioethanol dehydration process.