ABSTRACT
Abrasive water jet machining has become an indispensable process for cutting Kevlar fiber-reinforced polymers used in applications such as ballistics protection, race cars, and protective gloves. The complex and diffuse action of a large number of input parameters leads to the need to evaluate the quality characteristics of the technological transformation as a result of the deployment of experimental studies adapted to the specific processing conditions. Thus, the paper focuses on identifying the influence of different factors and modeling their action on the characteristics that define the quality of the cut parts, such as the kerf taper angle and the Ra roughness parameter, by applying statistical methods of design and analysis of experiments.
ABSTRACT
In the present study are depicted valuable observations for practitioners, obtained from an in vitro study which aims to evaluate the compressive strength of occlusal veneers fabricated from 3 type of restorative materials, before and after 1 month of acidic artificial saliva exposure (pH = 2.939). In this context, 90 extracted human molars were prepared to receive computer-aided design/computer-aided manufacturing (CAD/CAM) occlusal veneers. The restorative materials considered in this study were: Cerasmart; Straumann Nice and Tetric CAD. The occlusal veneers were designed, milled and cemented with an adhesive dual-cure resin cement. From all the extracted human molars, only sixty specimens were immersed in acidic artificial saliva, for 1 month, at 37 °C ± 1 °C and part of this specimens were also thermo-cycled, between 5 and 55 °C ± 2 °C, before compressive strength test. The results showed a lower compressive strength for both the samples exposed to acidic artificial saliva as well as for the samples exposed to acidic artificial saliva and thermo-cycled. Scanning electron microscopy (SEM) showed that after compressive strength, all the specimens non-exposed to acidic artificial saliva, present extensive cracks formation at the surface of the restorations, and after exposure to acidic artificial saliva for 1 month, the surface damage was characterized by longitudinal and profound fractures of the restoration, as well as the fracture of the tooth structure. Between CAD/CAM materials tested, nanoceramic resin shows more favorable fracture patterns, both before and after acidic artificial saliva exposure.
Subject(s)
Ceramics , Dental Porcelain , Humans , Compressive Strength , Saliva , Saliva, Artificial , Materials Testing , Dental Materials , Computer-Aided Design , Dental Stress AnalysisABSTRACT
The objective of this study was to evaluate the influence of hydrofluoric acid (HF) and conditioning time on the micro-shear bond strength (µSBS) between dual-cure resin cement and glass-ceramic materials, such as lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent) (EX) and leucite-reinforced ceramic (IPS Empress CAD, Ivoclar Vivadent) (EP), and also a hybrid ceramic (Vita Enamic, Vita Zahnfabrik) (VE). Eighteen sections with 1 mm thickness were cut from each CAD/CAM material and randomly divided into three groups, according to the surface etching time (30 s, 60 s, 90 s). The surface treatment was performed using 9.5% HF acid gel, then resin cement was applied on the prepared ceramic plates and light cured. µSBS values between resin cement and the ceramic material were measured with a universal testing machine at a crosshead speed of 0.5 mm/min until the failure occurred. The fractured surfaces of specimens were microscopically evaluated, and failure modes were classified as: adhesive between resin cement and ceramic, cohesive within ceramic or cement and mixed failure. Surface roughness of etched samples was examined using a scanning electron microscope. Obtained data were statistically analysed using one-way analysis of variance (ANOVA) and Bonferroni post hoc test with a level of significance α = 0.05. The results of the statistical methods applied indicate that µSBS mean difference for leucite-reinforced ceramic (EP) was statistically significant (p < 0.05). However, µSBS values for hybrid ceramic (VE) and lithium disilicate ceramic (EX) were not affected, from a statistical point of view, by the conditioning time (p > 0.05).