ABSTRACT
Electrically-conductive epoxy nanocomposites (NCs) with improved mechanical and adhesive properties were achieved through the combined addition of poly(ε-caprolactone) (PCL) and carbon nanotubes (CNTs). Three different ionic liquids (ILs) were used as dual role agents, i.e., as both curing and dispersing agents. Regardless of the IL used, the epoxy/PCL matrix of the NCs showed a single-phase behaviour and similar glass transition (Tg) and crosslinking density (νe) values to the unfilled epoxy/PCL/IL systems. Although the CNTs were more poorly dispersed in the epoxy/PCL/CNT/IL NCs than in the reference epoxy/CNT/IL NCs, which led to slightly lower electrical conductivity values, the epoxy/PCL/CNT/IL NCs were still semiconductive. Their low-strain mechanical properties (i.e., flexural modulus and flexural strength) were similar or better than those of the reference epoxy/IL systems and their high-strain mechanical properties (i.e., deformation at break and impact strength) were significantly better. In addition, the positive effects of the PCL and the CNTs on the adhesive properties of the epoxy/IL system were combined. The substitution of ILs for traditional amine-based curing agents and biodegradable PCL for part of the epoxy resin represents an important advance on the road towards greater sustainability.
ABSTRACT
Good dispersion of carbon nanotubes (CNTs) together with effective curing were obtained in epoxy/CNT nanocomposites (NCs) using three different ionic liquids (ILs). Compared to conventional amine-cured epoxy systems, lower electrical percolation thresholds were obtained in some of the IL-based epoxy systems. For example, the percolation threshold of the trihexyltetradecylphosphonium dicyanamide (IL-P-DCA)-based system was 0.001 wt.%. The addition of CNTs was not found to have any significant effect on the thermal or low-strain mechanical properties of the nanocomposites, but it did improve their adhesive properties considerably compared to the unfilled systems. This study demonstrates that ILs can be used to successfully replace traditional amine-based curing agents for the production of electrically conductive epoxy/CNT NCs and adhesives, as a similar or better balance of properties was achieved. This represents a step towards greater sustainability given that the vapor pressure of ILs is low, and the amount needed to effectively cure epoxy resins is significantly lower than any of their counterparts.
ABSTRACT
In this work, ionic liquid (IL)-cured epoxy resins were modified by adding poly(ε-caprolactone) (PCL). Three different ILs were used in order to study how (a) the chemical structure of the ILs and (b) the PCL content affect the phase behaviour, microstructure, mechanical and adhesive properties. Regardless of the IL used or the PCL content, the obtained materials showed a single phase. The addition of PCL to the epoxy resin resulted in plasticizing of the network blends, lower glass transition temperatures (Tg), and crosslinking densities (νe). Low PCL contents did not have a significant impact on the mechanical properties. However, the adhesive properties improved significantly at low PCL contents. Higher PCL contents led to a significant increase in toughness, especially in the case of the imidazolium-based IL. The balance achieved between the mechanical and adhesive properties of these IL-cured epoxy/PCL blends constitutes an important step towards sustainability. This is because a biodegradable polymer (PCL) was used to substitute part of the epoxy resin, and the ILs-which are non-volatile and cure effectively at much lower contents-were used instead of conventional curing agents. Given the wide use of this kind of materials in the adhesive industry, the practical significance of these results must be emphasised.
ABSTRACT
: Epoxy/Polycaprolactone (PCL) blends cured with a conventional diamine (4,4'-diaminodiphenylmethane, DDM) and with different amounts of a disulfide containing diamine (4, 4´-dithioaniline, DSS) were prepared through melting. The curing process was studied by FTIR and differential scanning calorimetry (DSC) and the mechanical behavior of the networks was studied by DMA. The shape memory properties and the recyclability of the materials were also analyzed. All blends showed a very high curing degree and temperature activated shape memory effect, related to the glass transition of the epoxy resin. The PCL plasticized the mixture, allowing tailoring of the epoxy glass transition. In addition, in the blends cured with DSS, as a consequence of the disulfide exchange reaction, the permanent shape could be erased and a new shape could be reprogrammed. Using this strategy, reprogrammable permanent shape memory materials were obtained.