ABSTRACT
The laser treatment of surfaces enables the alteration of their morphology and makes them suitable for various applications. This paper discusses the use of a laser beam to develop surface features that enhance pool boiling heat transfer. Two types of structures (in the 'macro' and 'micro' scale) were created on the samples: microfins (grooves) and surface roughness. The impact of the pulse duration and scanning velocity on the height of the microfins and surface roughness at the bottom of the grooves was analyzed with a high precision optical profilometer and microscope. The results indicated that the highest microfins and surface roughness were obtained with a pulse duration of 250 ns and scanning velocity of 200 mm/s. In addition, the influence of the 'macro' and 'micro' scale modifications on the boiling heat transfer of distilled water and ethyl alcohol was studied on horizontal samples heated with an electric heater. The largest enhancement was obtained for the highest microfins and roughest surfaces, especially at small superheats. Heat flux dissipated from the samples containing microfins of 0.4 mm height was, maximally, over three times (for water) and two times (for ethanol) higher than for the samples with smaller microfins (0.2 mm high). Thus, a modification of a selected model of boiling heat transfer was developed so that it would be applicable to laser-processed surfaces. The correlation proved to be quite successful, with almost all experimental data falling within the ±100% agreement bands.
ABSTRACT
Analysis of the geometrical structure of the surface of materials is an issue already widely recognised and included in international standards. The authors present the possibilities of extending the analysis of the coatings' geometrical structure through X-ray nanotomography imaging, three-dimensional image processing, and stereological methods. Analysis of the state of the art reveals that there are no scientific rapports (indexed by Scopus) on the application X-ray nanotomography for analysis of the geometry of a coating. The presented study shows that this imaging technique can be applied and provide additional information on the quality of the layer. The comparative tests were carried out on samples with a cermet coating before and after laser treatment, including standard tests of the surface geometry and the analysis of three-dimensional images obtained from nanotomography. A set of parameters describing the compactness and thickness distribution of the applied coating is proposed, which facilitates the qualitative assessment of the application process and improvements through the additional processing of technological layers. The obtained results show that although the average thickness values before and after laser treatment did not differ significantly, their distribution on the sample surface was different, as presented in the visualisation. The determined stereological parameter NV (number of objects per unit volume) allowed for the assessment of the layer compactness, and as the analyses showed, this value decreased by more than two times after laser treatment. The analysis of the degree of sample coverage by the cermet layer showed that it increased from 70% to 95% after laser treatment, which confirms the treatment's positive effect on the layer's quality. This research shows that three-dimensional analysis significantly enriches the information about the geometry of the surface layer, providing data which other research techniques are unable to acquire.
ABSTRACT
A characteristic feature of sintered stainless steel (SSS) is its porosity. Porosity results in a lower density of steel, making attractive components for producing lightweight structures and materials used in industry (e.g., the automotive industry or aerospace). Scientists also observe that porosity adversely affects steel's properties, especially its strength properties. One of the proposals for improving the discussed properties is the use of surface treatment of sintered stainless steels, e.g., with the use of concentrated energy sources such as plasma beams or laser beams. However, this proposal is an incidental subject of research, which is not justified from the point of view of the obtained research results presented by a few research groups. In this study, the surface modification (surface treatment) of sintered stainless steel was presented. The authors proposed the use of two surface treatments in order to compare them and obtain the best results. The first treatment was the deposit of Cr3C2-NiCr coatings on SSS surfaces using the atmospheric plasma spraying (APS) method. The second treatment was to create surface layers on SSSs by laser alloying the surface with a CO2 laser. Due to high precision and ease of automation, the most common methods in surface alloying treatment are laser technologies. This research's main aim was to analyze the microstructure and strength properties of the SSS surface layer. The research confirms that applying the Cr3C2-NiCr coating and modifying the surface layer through the laser alloying method improves the mechanical properties of SSSs.
ABSTRACT
The main objective of the present work is to determine the effects of laser processing on properties of WC-Co electro-spark deposited (ESD) coatings on steel substrates. Tungsten carbide coatings have been applied to steel substrates using a manual electrode feeder, model EIL-8A. The laser beam processing (LBP) of electro-spark coatings was performed using an Nd:YAG fiber laser. The microstructure and properties of laser treated/melted coatings were evaluated by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), surface geometric structure (SGS) and roughness measurements and adhesion, microhardness, residual stresses, corrosion resistance and application tests. The obtained experimental data were subjected to statistical analysis and multidimensional numerical and visual exploratory techniques. It has been shown conclusively that the laser-treated ESD WC-Co coatings are characterized by lower microhardness, higher resistance to corrosion, increased roughness and better adhesion to the substrate. LBP homogenizes the chemical composition, refines the microstructure and heals microcracks and pores of ESD coatings. The laser treated ESD WC-Co coatings can be used in frictional sliding nodes (e.g., on the front seal rings used in pumps) and as protective layers.
ABSTRACT
Electro-spark deposition (ESD) and laser beam machining (LBM) are the technologies using the concentrated energy flux. This paper deals with the issue of the impact of laser modification on the morphology and mechanical properties of carbide/copper coatings produced by electro-spark treatment. The coatings were applied to C45 carbon steel samples using the EIL-8A device. The following three types of electrodes made using the powder metallurgy (PM) hot pressing technique, from copper and tungsten carbide powders of different percentage compositions, were used for the coatings: 25% WC and 75% Cu; 50% WC and 50% Cu; and 75% WC and 25% Cu. Laser modification of the surface layers was performed with an Nd:YAG laser. The research focused on the analysis of the morphology of coatings applied by electro-spark technology before and after laser processing. The analysis of the morphology of electro-spark coatings revealed that the coatings had microcracks and pores. The laser beam machining of ESD coatings led to the homogenization of chemical composition, fragmentation of the structure, and elimination of microcracks. In addition, measurements of porosity, microhardness, adhesion, and analysis of XRD phase composition of the electro-spark coatings were performed. Laser processing proved to have a positive effect on improving the adhesion of coatings and reducing their porosity. This paper also presents a simulation model of heat transfer processes for the case of laser radiation impact on a WC-Cu coating. The developed numerical model, describing the influence of laser treatment on the distribution of temperature fields in the heated material (at a given depth) is of significant importance in the development of treatment technologies. Laser-modified ESD coatings perform anti-wear and protective functions, which enable their potential application in means of transport such as rolling stock.