Influence of TiO2 nanoparticles content as reinforce material to enhance the mechanical and corrosion resistance properties of Sn and Sn-Ag alloy for dental applications.

This study evaluated the influence of the TiO2 nanoparticles (NPs) on the mechanical and chemical performance of Sn and Sn-Ag alloys. The XRD (X-ray diffraction) and HR-TEM (high resolution-transmission electron microscopy) methods were used to characterize the NPs synthesized by the sol-gel microwave process. The chemical composition of the alloys was Sn, Sn+3TiO2 NPs, Sn-5Ag+1.5TiO2 NPs, Sn-10Ag, and Sn-10Ag+3TiO2 NPs, obtained from an experimental factorial design (EFD). A statistical model was used to determine the mechanical and chemical properties, showing the Vickers hardness response surface, tensile strength, wear, and corrosion resistance. The wear and corrosion tests for the various alloy compositions were performed using human artificial saliva solution. The results indicated that the Sn-10Ag+3TiO2 NPs exhibited the highest mechanical performance due to their increased hardness (380 HV), tensile strength (370 N), and wear resistance (0.34 × 10-3 mm3 Nm-1); in all the cases, the inclusion of TiO2 NPs enhanced the corrosion resistance of the alloys. According to the American Dental Association (ADA), Sn-10Ag+3TiO2 NPs alloy could be classified as a possible type IV restorative material.

Green chemistry synthesis of nano-cuprous oxide.

Green chemistry and a central composite design, to evaluate the effect of reducing agent, temperature and pH of the reaction, were employed to produce controlled cuprous oxide (Cu2O) nanoparticles. Response surface method of the ultraviolet-visible spectroscopy is allowed to determine the most relevant factors for the size distribution of the nanoCu2O. X-ray diffraction reflections correspond to a cubic structure, with sizes from 31.9 to 104.3 nm. High-resolution transmission electron microscopy reveals that the different shapes depend strongly on the conditions of the green synthesis.