Additive Manufacturing Polyurethane Acrylate via Stereolithography for 3D Structure Polymer Electrolyte Application.

Additive manufacturing (AM), also known as 3D-printing technology, is currently integrated in many fields as it possesses an attractive fabrication process. In this work, we deployed the 3D-print stereolithography (SLA) method to print polyurethane acrylate (PUA)-based gel polymer electrolyte (GPE). The printed PUA GPE was then characterized through several techniques, such as Fourier transform infrared (FTIR), electrochemical impedance spectroscopy (EIS), X-ray diffraction analysis (XRD), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and scanning electron microscope (SEM). The printed GPE exhibited high ionic conductivity of 1.24 × 10-3 S cm-1 at low-lithium-salt content (10 wt.%) in ambient temperature and favorable thermal stability to about 300 °C. The FTIR results show that addition of LiClO4 to the polymer matrix caused a shift in carbonyl, ester and amide functional groups. In addition, FTIR deconvolution peaks of LiClO4 show 10 wt.% has the highest amount of free ions, in line with the highest conductivity achieved. Finally, the PUA GPE was printed into 3D complex structure to show SLA flexibility in designing an electrolyte, which could be a potential application in advanced battery fabrication.

Silver Nanoparticles Embedded on Reduced Graphene Oxide@Copper Oxide Nanocomposite for High Performance Supercapacitor Applications.

In this work, silver (Ag) decorated reduced graphene oxide (rGO) coated with ultrafine CuO nanosheets (Ag-rGO@CuO) was prepared by the combination of a microwave-assisted hydrothermal route and a chemical methodology. The prepared Ag-rGO@CuO was characterized for its morphological features by field emission scanning electron microscopy and transmission electron microscopy while the structural characterization was performed by X-ray diffraction and Raman spectroscopy. Energy-dispersive X-ray analysis was undertaken to confirm the elemental composition. The electrochemical performance of prepared samples was studied by cyclic voltammetry and galvanostatic charge-discharge in a 2M KOH electrolyte solution. The CuO nanosheets provided excellent electrical conductivity and the rGO sheets provided a large surface area with good mesoporosity that increases electron and ion mobility during the redox process. Furthermore, the highly conductive Ag nanoparticles upon the rGO@CuO surface further enhanced electrochemical performance by providing extra channels for charge conduction. The ternary Ag-rGO@CuO nanocomposite shows a very high specific capacitance of 612.5 to 210 Fg-1 compared against rGO@CuO which has a specific capacitance of 375 to 87.5 Fg-1 and the CuO nanosheets with a specific capacitance of 113.75 to 87.5 Fg-1 at current densities 0.5 and 7 Ag-1, respectively.