Optimizing electric corona treatment for hydroxypropylated starch-based coatings.

The aim of this investigation was to determine the role of negative direct current and alternating current (plasma) corona treatments in modification of bio-based dispersion barrier coatings and the response of replacing fossil-based binder with a thermoplastic bio-based binder (starch). The study emphasizes the importance of understanding and optimizing electric corona discharge in order to obtain high oxidation level without harming the substrate and causing unintentional treatment of the reverse side. The coatings were exposed to different corona treatment conditions using a novel developed sheet-fed laboratory-scale device. Corona-induced topographical, mechanical and surface chemical changes were observed from atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), and contact angle and surface energy measurements. XPS results indicated further that partial starch decomposition occurred after plasma treatment. Coated surfaces became substantially smoother after both treatments suggesting that nanoparticle migration and re-orientation effects occurred. Additionally, reverse side effects and strike through were also discussed.

Structure and Transport Properties of Mixed-Matrix Membranes Based on Polyimides with ZrO2 Nanostars.

Mixed-matrix membranes based on amorphous and semi-crystalline polyimides with zirconium dioxide (ZrO2) nanostars were synthesized. Amorphous poly(4,4'-oxydiphenylenepyromellitimide) and semi-crystalline polyimide prepared from 1,4-bis(4-aminophenoxy)benzene and 4,4'-oxydiphthalic anhydride were used. The effect of ZrO2 nanostars on the structure and morphology of nanocomposite membranes was studied by wide-angle X-ray scattering, scanning electron microscopy, atomic force microscopy, and contact angle measurements. Thermal properties and stability were investigated by thermogravimetric analysis and differential scanning calorimetry. Transport properties of hybrid membranes containing 5 wt % ZrO2 were tested for pervaporation of a mixture of butanol⁻water with 10 wt % H2O content. It was found that a significant amount of the ZrO2 added to the semi-crystalline polyimide is encapsulated inside spherulites. Therefore, the beneficial influence of inorganic filler on the selectivity of mixed-matrix membrane with respect to water was hampered. Mixed-matrix membranes based on amorphous polymer demonstrated the best performance, because water molecules had higher access to inorganic particles.