ABSTRACT
Swellable polymer microspheres that respond to pH were prepared by free radical dispersion polymerization using N-isopropylacrylamide (NIPA), N,N'-methylenebisacrylamide (MBA), 2,2-dimethoxy-2-phenylacetylphenone, N-tert-butylacrylamide (NTBA), and a pH-sensitive functional comonomer (acrylic acid, methacrylic acid, ethacrylic acid, or propacrylic acid). The diameter of the microspheres was between 0.5 and 1.0 µm. These microspheres were cast into hydrogel membranes prepared by mixing the pH-sensitive swellable polymer particles with aqueous polyvinyl alcohol (PVA) solutions followed by crosslinking with glutaric dialdehyde for use as pH sensors. Large changes in the turbidity of the PVA membrane were observed as the pH of the buffer solution in contact with the membrane was varied. These changes were monitored by UV-visible absorbance spectroscopy. Polymer swelling of many NIPA copolymers was reversible and independent of the ionic strength of the buffer solution in contact with the membrane. Both the degree of swelling and the apparent pKa of the polymer microspheres increased with temperature. Furthermore, the apparent pKa of the polymer particles could be tuned to respond sharply to pH in a broad range (pH 4.0-7.0) by varying the amount of crosslinker (MBA) and transition temperature modifier (NTBA), and the amount, pKa, and hydrophobicity of the pH-sensitive functional comonomer (alkyl acrylic acid) used in the formulation. Potential applications of these polymer particles include fiber optic pH sensing where the pH-sensitive material can be immobilized on the distol end of an optical fiber.
Subject(s)
Hydrogels , Polymers , Acrylamides , Hydrogen-Ion Concentration , MicrospheresABSTRACT
Lightly crosslinked theophylline imprinted polyN-(N-propyl)acrylamide particles (ca. 300nm in diameter) that are designed to swell and shrink as a function of analyte concentration in aqueous media were spin coated onto a gold surface. The nanospheres responded selectively to the targeted analyte due to molecular imprinting. Chemical sensing was based on changes in the refractive index of the imprinted particles that accompanied swelling due to binding of the targeted analyte, which was detected using surface plasmon resonance (SPR) spectroscopy. Because swelling leads to an increase in the percentage of water in the polymer, the refractive index of the polymer nanospheres decreased as the particles swelled. In the presence of aqueous theophylline at concentrations as low as 10(-6)M, particle swelling is both pronounced and readily detectable. The full scale response of the imprinted particles to template occurs in less than 10min. Swelling is also reversible and independent of the ionic strength of the solution in contact with the polymer. Replicate precision is less than 10(-4) RI units. By comparison, there is no response to caffeine which is similar in structure to theophylline at concentrations as high as 1x10(-2)M. Changes in the refractive index of the imprinted polymer particles, as low as 10(-4) RI units could be readily detected. A unique aspect of the prepared particles is the use of light crosslinking rather than heavy crosslinking. This is a significant development as it indicates that heavy crosslinking is not entirely necessary for selectivity in molecular imprinting with polyacrylamides.