ABSTRACT
Tm-Tb co-substituted Co-Ni nanospinel ferrites (NSFs) as (Co0.5Ni0.5) [TmxTbxFe2-2x]O4 (x = 0.00-0.05) NSFs were attained via the ultrasound irradiation technique. The phase identification and morphologies of the NSFs were explored using X-rays diffraction (XRD), selected area electron diffraction (SAED), and transmission and scanning electronic microscopes (TEM and SEM). The magnetization measurements against the applied magnetic field (M-H) were made at 300 and 10 K with a vibrating sample magnetometer (VSM). The various prepared nanoparticles revealed a ferrimagnetic character at both 300 and 10 K. The saturation magnetization (Ms), the remanence (Mr), and magneton number (nB) were found to decrease upon the Tb-Tm substitution effect. On the other hand, the coercivity (Hc) was found to diminish with increasing x up to 0.03 and then begins to increase with further rising Tb-Tm content. The Hc values are in the range of 346.7-441.7 Oe at 300 K to 4044.4-5378.7 Oe at 10 K. The variations in magnetic parameters were described based on redistribution of cations, crystallites and/or grains size, canting effects, surface spins effects, super-exchange interaction strength, etc. The observed magnetic results indicated that the synthesized (Co0.5Ni0.5)[TmxTbxFe2-x]O4 NSFs could be considered as promising candidates to be used for room temperature magnetic applications and magnetic recording media.
ABSTRACT
Co0.5Ni0.5NbxFe2-xO4 (0.00 ≤ x ≤ 0.10) nanoparticles (NPs) were prepared using the hydrothermal approach. The X-ray powder diffraction (XRD) pattern confirmed the formation of single-phase spinel ferrite. The crystallite size was found to range from 18 to 26 nm. The lattice parameters were found to increase with greater Niobium ion (Nb3+) concentration, caused by the variance in the ionic radii between the Nb3+ and Fe3+. Fourier transform infrared analysis also proved the existence of the spinal ferrite phase. The percent diffuse reflectance (%DR) analysis showed that the value of the band gap increased with growing Nb3+ content. Scanning electron microscopy and transmission electron microscopy revealed the cubic morphology. The magnetization analyses at both room (300 K, RT) and low (10 K) temperatures exhibited their ferromagnetic nature. The results showed that the Nb3+ substitution affected the magnetization data. We found that Saturation magnetization (Ms), Remanence (Mr), and the Magnetic moment ( n B ) decreased with increasing Nb3+. The squareness ratio (SQR) values at RT were found to be smaller than 0.5, which postulate a single domain nature with uniaxial anisotropy for all produced ferrites. However, different samples exhibited SQRs within 0.70 to 0.85 at 10 K, which suggests a magnetic multi-domain with cubic anisotropy at a low temperature. The obtained magnetic results were investigated in detail in relation to the structural and microstructural properties.
ABSTRACT
We have briefly reviewed the occurrence of the post-synaptic potentials between neurons, the relationship between EEG and neuron dynamics, as well as methods of signal analysis. We propose a simple stochastic model representing electrical activity of neuronal systems. The model is constructed using the Monte Carlo simulation technique. The results yielded EEG-like signals with their phase portraits in three-dimensional space. The Lyapunov exponent was positive, indicating chaotic behavior. The correlation of the EEG-like signals was.92, smaller than those reported by others. It was concluded that this neuron model may provide valuable clues about the dynamic behavior of neural systems.