Use of Acid for Oxide Layer Removal of Overcast UCLA Abutments: Influence on Fit and Roughness.

PURPOSE: The objective of this study was to evaluate the influence of the oxide layer removal procedure using acid on the roughness and internal fit of overcast universal castable long abutments (UCLAs) for a taper connection. MATERIALS AND METHODS: For this, maxillary first premolars were waxed on the plastic sleeve of 15 UCLAs with a premachined interface. The specimens were overcast using the NiCr alloy, and the frameworks were randomly distributed to undergo one of two different oxide layer removal methods: blasting with 100-µm particles of aluminum oxide at 0.60-MPa pressure or bathing for 5 hours in 0.5% hydrofluoric acid. The surface roughness was evaluated by a light interferometer at the subcritical contour of each abutment. Next, the frameworks were attached to the respective analogs for internal fit evaluation. The central cross section of each assembly was exposed, and three regions were visualized by scanning electron microscopy (SEM): taper interface, axial wall, and index region. The premachined base was used as the control. The groups were compared using analysis of variance (ANOVA) and Tukey post hoc test (α = .05). RESULTS: The results showed that acid bathing produced intermediary roughness between premachined and blasted surfaces (P < .05). SEM images showed a sealed interface at the taper region of all groups, despite some irregularities after alumina blasting. Increased discrepancies at the axial wall and index region were found after the alumina blasting procedure (P < .05). CONCLUSION: It was concluded that acid bathing should be used, instead of blasting to remove the oxide layer, to produce a better fit and smoother surface on UCLAs.

Influence of luting space of zirconia abutment on marginal discrepancy and tensile strength after dynamic loading.

STATEMENT OF PROBLEM: Although luting space is related to the marginal fit of indirect restorations, information on its influence on the marginal fit and tensile strength of zirconia abutments bonded to titanium bases is lacking. PURPOSE: The purpose of this in vitro study was to evaluate the influence of luting space on the marginal discrepancy and tensile strength of zirconia abutments bonded to a titanium base after dynamic loading. MATERIAL AND METHODS: Ninety implant replicas were embedded in resin blocks to attach 4-mm-high titanium luting bases. Zirconia abutments (Ceramill Zolid FX) were fabricated with different internal luting spaces: 25 µm (G25), 50 µm (G50), or 75 µm (G75). The zirconia abutments were cemented on the titanium bases by using a resin cement (Panavia F 2.0) under a constant load of 20 N. The marginal discrepancy and internal fit of 10 random specimens from each group were evaluated with a stereoscopic microscope at ×50 magnification. The remaining specimens were submitted to the tensile strength test in which half were evaluated after dynamic loading (1.2 million cycles of 200 N at 3.8 Hz) in a mechanical fatigue machine. The tensile strength test was performed using a pullout apparatus coupled to a universal testing machine at a crosshead speed of 0.5 mm/min. The mode of failure was determined by observation at ×50 magnification under a stereomicroscope and classified into adhesive or mixed. The groups were compared by using 2-way ANOVA and the Tukey HSD test (α=.05). RESULTS: Increase in the luting space did not influence the marginal discrepancy (P>.05). All zirconia abutments exhibited lower pullout strength after fatigue simulation (P<.05). G75 demonstrated lower tensile strength than G25 and G50 before and after loading (P<.05). Most failures were adhesive at the zirconia-cement interface. CONCLUSIONS: The increase of the luting space to 75 µm did not influence marginal discrepancy; however, it reduced the tensile strength of a zirconia abutment bonded to a titanium base.

Fluxo de trabalho digital para a reabilitação estética dos dentes anteriores / Digital workflow for the esthetic restoration of anterior teeth

Os métodos digitais atualmente disponíveis para o planejamento e fabricação das restaurações permitem padronização e melhor previsibilidade para os resultados funcionais e estéticos finais. A qualidade atual dos equipamentos digitais disponíveis melhorou a qualidade dos processos de confecção e possibilita que o número de sessões clínicas seja reduzido. Este artigo irá descrever a restauração dos 6 dentes superiores anteriores de paciente insatisfeita com o aspecto estético inicial do seu sorriso. O planejamento e confecção das restaurações propostas foram realizados com auxílio dos métodos digitais disponíveis atualmente. Os dentes foram todos restaurados com coroas totais fabricadas em dissilicato de lítio. Pôde-se concluir que o domínio do fluxo de trabalho digital permite maior padronização no planejamento e fabricação das restaurações estéticas, possibilitando resultados previsíveis e maior sucesso clínico. A melhor comunicação com o paciente e a menor quantidade de sessões clínicas necessárias para o tratamento completo do paciente são grandes vantagens do tratamento digital. Já o custo elevado dos equipamentos ainda é uma desvantagem, mas seu progressivo barateamento irá permitir cada vez mais seu uso na clínica diária.

The methods currently available for digital planning and manufacturing of restorations allow more standardized and predictable functional and esthetic outcomes. The current state of the art of digital equipment improved the manufacturing procedures and allowed the reduction of clinical sessions needed for complete patient treatment. This article will describe the restoration of 6 anterior maxillary teeth of a patient unsatisfied with her smile esthetics. The planning and manufacturing of restorations were all conducted by using the currently available digital methods. All teeth were restored with lithium disilicate crowns. It could be concluded that the digital workflow allows more standardization in planning and manufacturing restorations, allowing more predictable results and highly successful outcomes. The best communication with the patient and the reduced number of clinical sessions are great advantages of the digital treatment. however the high costs of equipment is still a disadvantage, but a possible future cost reduction will allow its increased use in daily clinical practice.

Zircônia translúcida associada ao planejamento digital de restaurações monolíticas implantossuportadas / Translucent zirconia associated with the virtual design of monolithic implant-supported restorations

A utilização dos sistemas digitais aumentou consideravelmente na Odontologia e está cada dia mais acessível. Relatos de sucesso com o uso de restaurações cerâmicas livres de metal também são mais constantes. Os sistemas digitais trazem novas possibilidades de planejamento e fabricação para as restaurações cerâmicas, além de aumentar a previsibilidade dos tratamentos devido à visualização virtual da restauração que será fabricada. Atualmente, a zircônia translúcida associada à caracterização extrínseca, na forma de coroas monolíticas, permite resultados altamente estéticos e apresenta resistência adequada para a aplicação segura em dentes posteriores. O presente artigo teve como objetivo apresentar um caso clínico no qual o primeiro molar inferior direito foi restaurado com uma coroa monolítica em zircônia translúcida, obtida por tecnologia CAD/CAM e maquiada por caracterização extrínseca.

The application of digital dentistry has grown and seems more avalilable in dentistry. Reports of clinical success are constant. Digital dentistry allows clinicians to design and fabricate predictable restorations for daily clinics. The virtual design of the restoration is also an excellent tool to predict the final outcome of the rehabilitation by the patient, thus leading to more predictable and esthetically successful outcomes. Monolithic translucent zirconia associated with external staining allows highly esthetic results and with adequate fracture strength for the use in posterior teeth. This study will describe the restoration of a mandible first molar with the aid of digital impression, and virtual planning and CAD/CAM fabrication of the restoration. The restoration was fabricated by using monolithic translucent zirconia and characterized with external staining.

Técnica laboratorial para condicionamento superficial de restaurações cerâmicas

Ao se realizar a cimentação de restaurações indiretas, independente do material que compõe a restauração, suas superfícies internas devem ser limpas e/ou condicionadas. Os tratamentos superficiais indicados para dentes e restaurações cerâmicas são distintos como descrito por Oztürk E. e cols2. Até mesmo dentro da família das restaurações cerâmicas, dependendo da sua composição específica, tratamentos diferentes devem ser realizados, seguindo sempre as recomendações dos fabricantes. De modo geral, a superfície interna das restaurações pode necessitar de tratamento mecânico e químico, o que pode ocorrer através de jateamento com óxido de alumínio, ácido Fluorídrico, silanização e/ou sistemas adesivos3. A força de adesão entre o substrato cerâmico e os cimentos resinosos é sensível a muitas variáveis como o tipo de cimento utilizado e ao método empregado no tratamento da superfície1. A fim de se evitar que este condicionamento atinja superfícies onde não se deseja adesão do cimento ou comprometa a lisura superficial da restauração, deve-se criar barreiras que impeçam tal intercorrência.O objetivo deste artigo é descrever uma técnica de condicionamento superficial em uma restauração indireta em cerâmica, utilizando barreira em silicone, técnica que pode ser realizada em ambiente clínico e/ou laboratorial

Reabilitação protética de paciente edêntulo após maxilectomia: um caso clínico / Prosthetic rehabilitation of edentulous patient after maxillectomy: a clinical report

Apesar de todos os avanços tecnológicos na realidade socioeconônica em que vivemos, tanto a reabilitação protética implanto-retida quanto a realização rotineira de exames caros como Tomografias Computadorizadas (TCs) e Imagem por Ressonância Magnética (IRMs) são restritas a uma parcela muito pequena da população, dando origem muitas vezes a casos de pacientes que sofreram maxilectomia há mais de 20 anos sem nunca terem sido reabilitados, sobrevivendo à margem da sociedade. Este artigo tem como objetivo apresentar um caso clínico, descrevendo uma técnica simples e acessível de reabilitação de pacientes submetidos à maxilectomia através da confecção de próteses totais obturadoras

Resistência ao cisalhamento da colagem do aço inoxidável austenítico ao esmalte bovino utilizando Transbond XT© e o primer MIP / Shear bond strenght in bonding of stainless steel austenitic to bovine enamel using Transbond XT© and primer MIP

A evolução dos materiais dentários utilizados para colagem em Ortodontia vem facilitando os procedimentos nesta área. Entretanto, uma das dificuldades encontradas pelos ortodontistas é o controle da umidade no ato da colagem. Por este motivo, buscamos um material que tivesse adesão à estrutura dentária em meio úmido, compatível com as necessidades clínicas. O objetivo deste trabalho foi avaliar a resistência ao cisalhamento da colagem de estruturas metálicas (aço inoxidável 303 austenítico, de que são feitos os bráquetes da Morelli) em esmalte bovino utilizando o cimento resinoso Transbond XT, associado ou não ao Transbond MIP "primer" hidrófilo em presença ou não de umidade. Foram criados 3 grupos, sendo eles: A) Transbond XT (KIT), em meio seco; B)Transbond MIP "primer" hidrófilo aplicado no esmalte, em meio úmido; C)Transbond XT (KIT) + Transbond MIP "primer" hidrófilo aplicado no esmalte e primer/adesivo aplicado no metal, em meio úmido. Como resultado do teste de resistência ao cisalhamento, obtivemos como média (valores em Kgf/cm2): A) 56,31; B)97,63; C)44,12. Sendo assim, concluímos que o cimento resinoso Transbond XT, quando associado ao MIP "primer" hidrófilo em presença de umidade, tem aumentada sua resistência ao cisalhamento