ABSTRACT
The topography and chemical composition modification of titanium (Ti) implants play a decisive role in improving biocompatibility and bioactivity, accelerating osseointegration, and, thus, determining clinical success. In spite of the development of surface modification strategies, bacterial contamination is a common cause of failure. The use of systemic antibiotic therapy does not guarantee action at the contaminated site. In this work, we proposed a surface treatment for Ti implants that aim to improve their osseointegration and reduce bacterial colonization in surgery sites due to the local release of antibiotic. The Ti discs were hydrothermally treated with 3M NaOH solution to form a nanostructured layer of titanate on the Ti surface. Metronidazole was impregnated on these nanostructured surfaces to enable its local release. The samples were coated with poly(vinyl alcohol)-PVA films with different thickness to evaluate a possible control of drug release. Gamma irradiation was used to crosslink the polymer chains to achieve hydrogel layer formation and to sterilize the samples. The samples were characterized by XRD, SEM, FTIR, contact angle measurements, "in vitro" bioactivity, and drug release analysis. The alkaline hydrothermal treatment successfully produced intertwined, web-like nanostructures on the Ti surface, providing wettability and bioactivity to the Ti samples (Ti + TTNT samples). Metronidazole was successfully loaded and released from the Ti + TTNT samples coated or not with PVA. Although the polymeric film acted as a physical barrier to drug delivery, all groups reached the minimum inhibitory concentration for anaerobic bacteria. Thus, the surface modification method presented is a potential approach to improve the osseointegration of Ti implants and to associate local drug delivery with dental implants, preventing early infections and bone failure.
ABSTRACT
This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.
Subject(s)
Bisphenol A-Glycidyl Methacrylate/chemistry , Ceramics/chemistry , Polyethylene Glycols/chemistry , Polymethacrylic Acids/chemistry , Resin Cements/chemistry , Analysis of Variance , Light-Curing of Dental Adhesives/methods , Materials Testing , Reference Values , Reproducibility of Results , Self-Curing of Dental Resins/methods , Tensile StrengthABSTRACT
Abstract This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.
Subject(s)
Polyethylene Glycols/chemistry , Polymethacrylic Acids/chemistry , Ceramics/chemistry , Bisphenol A-Glycidyl Methacrylate/chemistry , Resin Cements/chemistry , Reference Values , Tensile Strength , Materials Testing , Reproducibility of Results , Analysis of Variance , Self-Curing of Dental Resins/methods , Light-Curing of Dental Adhesives/methodsABSTRACT
O objetivo deste trabalho foi analisar a diferença na rugosidade superficial de três resinas compostas submetidas a ciclos de imersão em três soluções pigmentantes. A amostra foi dividida em 4 grupos, de acordo com o tipo de solução de imersão: no Grupo I, saliva artificial (controle); no Grupo II, café; no Grupo III, Coca-Cola®; e, no Grupo IV, café seguido de Coca-Cola®. Cada grupo foi dividido em 3 subgrupos (N=9) de cada tipo de resina. Os corpos-de-prova foram levados à estufa a 37ºC (±1ºC), mergulhados em saliva artificial e estocados por uma semana. Após esse procedimento, todas as amostras sofreram três ciclos diários de imersão durante um período de 30 dias, após o qual tiveram sua lisura superficial avaliada no rugosímetro (Ra). Após a análise dos resultados pôde-se concluir que as imersões em Coca-Cola® e em Café e Coca-Cola® diminuem significativamente a rugosidade em todos os materiais, e a imersão em Café aumentou a rugosidade na Durafil® e na Esthet X®. A corrosão pode ter sido o processo responsável pelo aumento na sua lisura superficial, conferido aos materiais após a imersão em Coca-Cola®.