Skin wound regeneration with bioactive glass-gold nanoparticles ointment.

The bioactive glasses can lead to the promotion of growth of granulation tissue, while the gold nanoparticles (AuNPs) can induce the acceleration of wound healing including tissue regeneration, connective tissue formation, and angiogenesis. The aim of this study was to evaluate the impact of using the bioactive glass (BG) and BG-AuNPs composites on skin wound healing in experimental rat models for 14 days. Sol-gel derived BGs and BG-AuNPs composites mixed with Vaseline at 6, 12 and 18 wt% were used to evaluate the repair response of the skin. During the process of healing, granulomatous reaction was observed in the wound treated with 12 and 18 wt% BG-Vaseline ointments. Furthermore, a strong vascular proliferation and complete wound regeneration were found in 18%BG-AuNPs-Vaseline treated groups. The results derived from the performed investigations revealed that the 18% BG-AuNPs-Vaseline ointment is a promising candidate for wound healing applications.

Novel bioactive glass-AuNP composites for biomedical applications.

The bioactive glasses doped with gold nanoparticles (AuNPs) are very attractive materials due to their potential in medical applications. In the present study Pluronic-nanogold hybrid nanoparticles were introduced during the sol-gel route of the SiO2-CaO-P2O5 glasses preparation. The obtained samples were characterized by UV-vis spectroscopy, X-ray diffraction, FT-IR spectroscopy, transmission electron and scanning electron microscopy and afterwards they were investigated in terms of bioactivity, protein adsorption and cells viability. The in vitro bioactivity assessment shows the increase of the number of agglomerated spherical shapes of apatite layers for all Au containing samples, but apatite like structure sizes are influenced by the AuNP content. Beside the spherical shapes, three-dimensional flower-like nanostructures were observed on the surface of the glass with 0.2mol% Au2O. Zeta potential and fluorescence spectroscopy measurements evidenced that the amount of serum albumin adsorbed onto the composites surface increases with the AuNP content. FT-IR measurements point out that the secondary structure of the adsorbed proteins presents few minor changes, indicating biocompatibility of the AuNP doped glasses. The good proliferation rate of Human keratinocytes cells obtained in the presence of samples with 0.15 and 0.2mol% Au2O is comparable with the values achieved from free AuNP, fact that proves the preservation of AuNP properties after their incorporation inside the bioactive glass matrices.

Bioactive and biocompatible copper containing glass-ceramics with remarkable antibacterial properties and high cell viability designed for future in vivo trials.

In the present study our interest is focused on finding the efficiency of 60SiO2·(32 - x)CaO·8P2O5·xCuO (mol%) glass-ceramics, with 0 ≤ x ≤ 4 mol%, in terms of bioactivity, biocompatibility, antibacterial properties and cell viability in order to determine the most appropriate composition for their further use in in vivo trials. The sol-gel synthesized samples show a preponderantly amorphous structure with a few crystallization centers associated with the formation of an apatite and calcium carbonate crystalline phases. The Fourier Transform Infrared (FT-IR) spectra revealed slightly modified absorption bands due to the addition of copper oxide, while the information derived from the measurements performed by transmission electron microscopy, UV-vis and electron paramagnetic resonance spectroscopy showed the presence of ions and metallic copper species. X-Ray photoelectron spectroscopic analysis indicated the presence of copper metallic species, in a reduced amount, only on the sample surface with the highest Cu content. Regarding in vitro assessment of bioactivity, the results obtained by X-ray diffraction, FT-IR spectroscopy and scanning electron microscopy, demonstrated the formation of a calcium phosphate layer on all investigated sample surfaces. The inhibitory effect of the investigated samples was more significant on the Pseudomonas aeruginosa than the Staphylococcus aureus strain, the sample with the lowest concentration of copper oxide (0.5 mol%) being also the most efficient in both bacterial cultures. This sample also exhibits a very good bactericidal activity, for the other samples it was necessary to use a higher quantity to inhibit and kill the bacterial species. The secondary structure of adsorbed albumin presents few minor changes, indicating the biocompatibility of the glass-ceramics. The cell viability assay shows a good proliferation rate on samples with 0.5 and 1.5 mol% CuO, although all glass-ceramic samples exhibited a good in vivo tolerance.