ABSTRACT
We synthesized pristine mica (Mica) and N-octadecyl-N'-octadecyl imidazolium iodide (IM) modified mica (Mica-IM), characterized it, and applied it at 0.1-5.0 wt.% loading to prepare epoxy nanocomposites. Dynamic differential scanning calorimetry (DSC) was carried out for the analysis of the cure potential and kinetics of epoxy/Mica and epoxy/Mica-IM curing reaction with amine curing agents at low loading of 0.1 wt.% to avoid particle aggregation. The dimensionless Cure Index (CI) was used for qualitative analysis of epoxy crosslinking in the presence of Mica and Mica-IM, while qualitative cure behavior and kinetics were studied by using isoconversional methods. The results indicated that both Mica and Mica-IM improved the curability of epoxy system from a Poor to Good state when varying the heating rate in the interval of 5-15 °C min-1. The isoconversional methods suggested a lower activation energy for epoxy nanocomposites with respect to the blank epoxy; thus, Mica and Mica-IM improved crosslinking of epoxy. The higher order of autocatalytic reaction for epoxy/Mica-IM was indicative of the role of liquid crystals in the epoxide ring opening. The glass transition temperature for nanocomposites containing Mica and Mica-IM was also lower than the neat epoxy. This means that nanoparticles participated the reaction because of being reactive, which decelerated segmental motion of the epoxy chains. The kinetics of the thermal decomposition were evaluated for the neat and mica incorporated epoxy nanocomposites epoxy with varying Mica and Mica-IM amounts in the system (0.5, 2.0 and 5.0 wt.%) and heating rates. The epoxy/Mica-IM at 2.0 wt.% of nanoparticle showed the highest thermal stability, featured by the maximum value of activation energy devoted to the assigned system. The kinetics of the network formation and network degradation were correlated to demonstrate how molecular-level transformations can be viewed semi-experimentally.
ABSTRACT
The epoxy/clay nanocomposites have been extensively considered over years because of their low cost and excellent performance. Halloysite nanotubes (HNTs) are unique 1D natural nanofillers with a hollow tubular shape and high aspect ratio. To tackle poor dispersion of the pristine halloysite (P-HNT) in the epoxy matrix, alkali surface-treated HNT (A-HNT) and epoxy silane functionalized HNT (F-HNT) were developed and cured with epoxy resin. Nonisothermal differential scanning calorimetry (DSC) analyses were performed on epoxy nanocomposites containing 0.1 wt.% of P-HNT, A-HNT, and F-HNT. Quantitative analysis of the cure kinetics of epoxy/amine system made by isoconversional Kissinger-Akahira-Sunose (KAS) and Friedman methods made possible calculation of the activation energy (Eα) as a function of conversion (α). The activation energy gradually increased by increasing α due to the diffusion-control mechanism. However, the average value of Eα for nanocomposites was lower comparably, suggesting autocatalytic curing mechanism. Detailed assessment revealed that autocatalytic reaction degree, m increased at low heating rate from 0.107 for neat epoxy/amine system to 0.908 and 0.24 for epoxy/P-HNT and epoxy/A-HNT nanocomposites, respectively, whereas epoxy/F-HNT system had m value of 0.072 as a signature of dominance of non-catalytic reactions. At high heating rates, a similar behavior but not that significant was observed due to the accelerated gelation in the system. In fact, by the introduction of nanotubes the mobility of curing moieties decreased resulting in some deviation of experimental cure rate values from the predicted values obtained using KAS and Friedman methods.
