ABSTRACT
Four different types of chitosan-based nanocomposite films were prepared using a solvent-casting method by incorporation with four types of nanoparticles, that is, an unmodified montmorillonite (Na-MMT), an organically modified montmorillonite (Cloisite 30B), a Nano-silver, and a Ag-zeolite (Ag-Ion). X-ray diffraction patterns of the nanocomposite films indicated that a certain degree of intercalation was formed in the nanocomposite films, with the highest intercalation in the Na-MMT-incorporated films followed by films with Cloisite 30B and Ag-Ion. Scanning electron micrographs showed that in all of the nanocomposite films, except the Nano-silver-incorporated one, nanoparticles were dispersed homogeneously throughout the chitosan polymer matrix. Consequently, mechanical and barrier properties of chitosan films were affected through intercalation of nanoparticles, that is, tensile strength increased by 7-16%, whereas water vapor permeability decreased by 25-30% depending on the nanoparticle material tested. In addition, chitosan-based nanocomposite films, especially silver-containing ones, showed a promising range of antimicrobial activity.
Subject(s)
Anti-Infective Agents , Chitosan , Food Packaging/instrumentation , Chemical Phenomena , Chemistry, Physical , Chitosan/chemistry , Solubility , Tensile Strength , WaterABSTRACT
"Green" nanocomposites have been successfully fabricated from cellulose acetate (CA) powder, eco-friendly triethyl citrate (TEC) plasticizer and organically modified clay. The effect of the amount of plasticizer varying from 15 to 40 wt % on the performance of the nanocomposites has been evaluated. The morphologies of these nanocomposites were evaluated through X-ray diffraction (XRD), atomic force microscopy (AFM), and transmission electron microscopy (TEM) studies. The mechanical properties of nanocomposites are correlated with the XRD and TEM observations. Cellulosic plastic-based nanocomposites with 20 wt % TEC plasticizer and 5 wt % organoclay showed better intercalation and an exfoliated structure than the counterpart having 30/40 wt % plasticizers. The tensile strength, modulus and thermal stability of cellulosic plastic reinforced with organoclay showed a decreasing trend with an increase of plasticizer content from 20 to 40 wt %. The nano-reinforcement at the lower volume fractions (phi < or = 0.02) reduced the water vapor permeability of cellulosic plastic by 2 times and the relative permeability better fits with larger platelet aspect ratios (alpha = 150).