Effect of Microwaves on the Rapid Curing of Metakaolin- and Aluminum Orthophosphate-Based Geopolymers.

This paper deals with the influence of microwaves on the hardening and curing of geopolymer binders synthesized from metakaolin or aluminum orthophosphate with sodium silicate solution as the activator. Pure geopolymer pastes as well as geopolymer mortars were considered. The variable parameters were the modulus of the sodium silicate solutions (molar ratio of SiO2 to Na2O: 1.5, 2.0 and 2.5) and the Si/Al ratio (3/1 and 2/1). Selected samples were cured in a microwave oven until hardening, so the curing time depended on the mixture. For comparison some samples were cured at ambient temperature. To investigate the influence of microwave radiation on the reaction kinetics, isothermal heat flow calorimetry, ultrasonic velocity measurements and rheological investigations into the variation of curing temperature were used. In addition, the mechanical properties of the cured samples were characterized. The results show that microwave curing only takes a few minutes, so it is the most time-saving method. Key factors influencing the geopolymer reaction under microwave radiation are the raw materials as well as the Si/Al ratio. Metakaolin-based geopolymer binders are more stable than those based on aluminum orthophosphate, especially regarding their salt efflorescence. Microwave radiation is an efficient method to accelerate the geopolymer reaction.

Investigations on Stability of Polycarboxylate Superplasticizers in Alkaline Activators for Geopolymer Binders.

Calcined clays are interesting starting materials to be used as SCMs (supplementary cementitious materials) in cements or to be converted to geopolymers by activation with a high alkaline activator. The adjustment of the properties in the fresh state, especially regarding the consistency of these binders, is almost exclusively achieved by the addition of water, since commercially available superplasticizers seem to be ineffective in low-calcium geopolymer systems. The aim of this study was a systematic investigation of various PCE (polycarboxylate ester/ether) superplasticizers (methacrylate ester PCE: MPEG, isoprenol ether PCE: IPEG, methallyl ether PCE: HPEG) with respect to their stability in different alkaline activators (NaOH, KOH, sodium and potassium silicate solutions). The effectiveness of superplasticizers (SPs) in low-calcium geopolymer binders was verified by rheological tests. Size exclusion chromatography was used to investigate if structural degradation of the superplasticizers occurs. The investigated PCE superplasticizers showed a thickening effect in the low-calcium geopolymer system. Depending on the alkalinity of the activator solution, a degradation process was detected for all the PCEs investigated. The side chains of the PCEs are cleaved off the backbone by basic ester and ether hydrolysis. The highest degree of degradation was found in sodium and potassium silicate solutions. In alkaline hydroxide solutions, the degradation process increases with increasing alkalinity.

Modified Carboxymethylcellulose-Based Scaffolds as New Potential Ecofriendly Superplasticizers with a Retardant Effect for Mortar: From the Synthesis to the Application.

This article is focused on the research and development of new cellulose ether derivatives as innovative superplasticizers for mortar systems. Several synthetic strategies have been pursued to obtain new compounds to study their properties on cementitious systems as new bio-based additives. The new water-soluble admixtures were synthesized using a complex carboxymethylcellulose-based backbone that was first hydrolyzed and then sulfo-ethylated in the presence of sodium vinyl sulphonate. Starting with a complex biopolymer that is widely known as a thickening agent was very challenging. Only by varying the hydrolysis times and temperatures of the reactions was achieved the aimed goal. The obtained derivatives showed different molecular weight (Mw) and anionic charges on their backbones. An improvement in shear stress and dynamic viscosity values of CEM II 42.5R cement was observed with the samples obtained with a longer time of higher temperature hydrolysis and sulfo-ethylation. Investigations into the chemical nature of the pore solution, calorimetric studies and adsorption experiments clearly showed the ability of carboxymethyl cellulose superplasticizer (CMC SP) to interact with cement grains and influence hydration processes within a 48-h time window, causing a delay in hydration reactions in the samples. The fluidity of the cementitious matrices was ascertained through slump test and preliminary studies of mechanical and flexural strength of the hardened mortar formulated with the new ecological additives yielded values in terms of mechanical properties. Finally, the computed tomography (CT) images completed the investigation of the pore network structure of hardened specimens, highlighting their promising structure porosity.

Formation of Geopolymers Using Sodium Silicate Solution and Aluminum Orthophosphate.

This paper reports the formation and structure of fast setting geopolymers activated by using three sodium silicate solutions with different modules (1.6, 2.0 and 2.4) and a berlinite-type aluminum orthophosphate. By varying the concentration of the aluminum orthophosphate, different Si/Al-ratios were established (6, 3 and 2). Reaction kinetics of binders were determined by isothermal calorimetric measurements at 20 °C. X-ray diffraction analysis as well as nuclear magnetic resonance (NMR) measurements were performed on binders to determine differences in structure by varying the alkalinity of the sodium silicate solutions and the Si/Al-ratio. The calorimetric results indicated that the higher the alkalinity of the sodium silicate solution, the higher the solubility and degree of conversion of the aluminum orthophosphate. The results of X-ray diffraction and Rietveldt analysis, as well as the NMR measurements, confirmed the assumption of the calorimetric experiments that first the aluminum orthophosphate was dissolved and then a polycondensation to an amorphous aluminosilicate network occurred. The different amounts of amorphous phases formed as a function of the alkalinity of the sodium silicate solution, indicate that tetrahydroxoaluminate species were formed during the dissolution of the aluminum orthophosphate, which reduce the pH value. This led to no further dissolution of the aluminum orthophosphate, which remained unreacted.