ABSTRACT
Wet ball milling was used for the synthesis of Cu2ZnSnSe4 (CZTSe) nanoparticles with a kesterite structure. The prepared nanoparticles were used for ink formulation. Surfactants and binders were added to improve the ink stability, prevent agglomeration, and enhance ink adhesion. The films deposited via spin coating were annealed at different temperatures using a rapid thermal processing system in the presence of selenium powder in an inert environment. Analytical techniques, such as X-ray diffraction, Raman spectroscopy, and Fourier-transform infrared spectroscopy, were used to confirm the formation of CZTSe nanoparticles with a single-phase, crystalline kesterite structure. Field-emission scanning electron microscopy and energy-dispersive X-ray spectroscopy were used to study the surface morphology and chemical composition of the thin films before and after annealing, with and without the sodium solution. The optoelectrical properties were investigated using ultraviolet-visible spectroscopy and Hall measurements. All the prepared CZTSe thin films exhibited a p-type nature with an optical bandgap in the range of 0.82-1.02 eV. The open-circuit voltage and fill factor of the CZTSe-based devices increased from 266 to 335 mV and from 37.79% to 44.19%, respectively, indicating a decrease in the number of recombination centers after Na incorporation.
ABSTRACT
In the present study, we adopt an easy and cost-effective route for preparing Cu2ZnSnS4 (CZTS)-absorber nanoparticles by a mechanochemical method using non-toxic and environmentally benign solvents (butanol, methyl ethyl ketone, and ethanol). The gram-scale synthesis of absorber nanoparticles was achieved in a non-hazardous, zero-waste process without using high-vacuum equipment. The effects of annealing and Na incorporation on the properties of spin-coated CZTS thin films were scrutinized. The deposited samples showed kesterite crystal structure and single phase. The morphological results revealed an improvement in the surface morphology after annealing. The optical bandgaps of the thin films lied in the range of 1.50-1.57 eV with p-type nature. Finally, photovoltaic devices were fabricated, and their cell performance parameters were studied. An efficiency of 0.16% was observed. The present study provides a potential route for the cost-effective fabrication of CZTS-based photovoltaic devices.