ABSTRACT
Fine-tuning of grain sizes can significantly influence the interaction between different dielectric phenomena, allowing the development of materials with tailored dielectric resistivity. By virtue of various synthesis mechanisms, a pathway to manipulate grain sizes and, consequently, tune the material's dielectric response is revealed. Understanding these intricate relationships between granulation and dielectric properties can pave the way for designing and optimizing materials for specific applications where tailored dielectric responses are sought. The experimental part involved the fabrication of dense BCT-BZT ceramics with different grain sizes by varying the synthesis (conventional solid-state reaction route and sol-gel) and consolidation methods. Both consolidation methods produced well-crystallized specimens, with Ba0.85Ca0.15O3Ti0.9Zr0.1 (BCTZ) perovskite as the major phase. Conventional sintering resulted in microstructured and submicron-structured BCT-BZT ceramics, with average grain sizes of 2.35 µm for the solid-state sample and 0.91 µm for the sol-gel synthesized ceramic. However, spark plasma sintering produced a nanocrystalline specimen with an average grain size of 67.5 nm. As the grain size decreases, there is a noticeable decrease in the maximum permittivity, a significant reduction in dielectric losses, and a shifting of the Curie temperature towards lower values.
ABSTRACT
A novel high-entropy perovskite powder with the composition Bi0.2K0.2Ba0.2Sr0.2Ca0.2TiO3 was successfully synthesized using a modified Pechini method. The precursor powder underwent characterization through Fourier Transform Infrared Spectroscopy and thermal analysis. The resultant Bi0.2K0.2Ba0.2Sr0.2Ca0.2TiO3 powder, obtained post-calcination at 900 °C, was further examined using a variety of techniques including X-ray diffraction, Raman spectroscopy, X-ray fluorescence, scanning electron microscopy, and transmission electron microscopy. Ceramic samples were fabricated by conventional sintering at various temperatures (900, 950, and 1000 °C). The structure, microstructure, and dielectric properties of these ceramics were subsequently analyzed and discussed. The ceramics exhibited a two-phase composition comprising cubic and tetragonal perovskites. The grain size was observed to increase from 35 to 50 nm, contingent on the sintering temperature. All ceramic samples demonstrated relaxor behavior with a dielectric maximum that became more flattened and shifted towards lower temperatures as the grain size decreased.
ABSTRACT
The phosphate KCoCr(PO4)2 and iron-substituted variants KCoCr1-xFex(PO4)2 (x = 0.25, 0.5, and 0.75) were synthesized by a solid-state reaction route, while a high substitution level of Fe was achieved. Their structures were refined using powder X-ray diffraction and indexed in a monoclinic system with a P21/n space group. A 3D framework with six-sided tunnels parallel to the [101] direction was formed in which the K atoms are located. Mössbauer spectroscopy confirms the exclusive presence of octahedral paramagnetic Fe3+ ions, with isomer shifts increasing slightly with x substitution. Electron paramagnetic resonance spectroscopy confirmed the presence of paramagnetic Cr3+ ions. The activation energy, determined by dielectric measurements, shows that the iron-containing samples present higher ionic activity. Relative to the electrochemical activity of K, these materials could be good candidates for positive and/or negative electrode materials for energy storage applications.