Fire behaviour of modern façade materials - Understanding the Grenfell Tower fire.

The 2017 Grenfell Tower fire spread rapidly around the combustible façade system on the outside of the building, killing 72 people. We used a range of micro- and bench-scale methods to understand the fire behaviour of different types of façade product, including those used on the Tower, in order to explain the speed, ferocity and lethality of the fire. Compared to the least flammable panels, polyethylene-aluminium composites showed 55x greater peak heat release rates (pHRR) and 70x greater total heat release (THR), while widely-used high-pressure laminate panels showed 25x greater pHRR and 115x greater THR. Compared to the least combustible insulation products, polyisocyanurate foam showed 16x greater pHRR and 35x greater THR, while phenolic foam showed 9x greater pHRR and 48x greater THR. A few burning drips of polyethylene from the panelling are enough to ignite the foam insulation, providing a novel explanation for rapid flame-spread within the facade. Smoke from polyisocyanurates was 15x, and phenolics 5x more toxic than from mineral wool insulation. 1 kg of burning polyisocyanurate insulation is sufficient to fill a 50m3 room with an incapacitating and ultimately lethal effluent. Simple, additive models are proposed, which provide the same rank order as BS8414 large-scale regulatory tests.

Structure⁻Property Studies on a New Family of Halogen Free Flame Retardants Based on Sulfenamide and Related Structures.

A wide variety of molecules containing S⁻N or S⁻N⁻S cores were synthesized, and their flame retardant properties in polypropylene (PP), low density polyethylene (LDPE) and polystyrene (PS) were investigated. In addition, polymers or oligomers bearing the sulfenamide functionality (SN) were also synthesized. It was shown that this radical generator family based on sulfenamides is very versatile in terms of structural modifications, and the thermal decomposition range can be easily adjusted by changing the R groups attached to the core. The thermal stabilities of the different sulfenamides were examined by thermogravimetric analysis (TGA). Radicals generated by the homolytic cleavage of the S⁻N or S⁻N⁻S bonds at an elevated temperature can effectively interact with the intermediate products of polymer thermolysis and provide excellent flame retardant properties. The choice of most suitable SN-structure varies depending on the polymer type. For polypropylene DIN 4102-1 B2 and UL94 VTM-2 classifications were achieved with only 0.5 to 1 wt % of sulfenamide, and, in some cases, no flaming dripping was observed. Also for LDPE thin films, sulfenamides offered the DIN 4102-1 B2 rating at low dosage. In the case of polystyrene, the very stringent UL94 V-0 classification was even achieved at a loading of 5 wt % of sulfenamide.