ABSTRACT
The effect of applied pressure on the magnetic properties of the Prussian blue analogue K0.4Fe4[Cr(CN)6]2.8 x 16 H2O (1) has been analyzed by dc and ac magnetic susceptibility measurements. Under ambient conditions, 1 orders ferromagnetically at a critical temperature (T(C)) of 18.5 K. Under application of pressure in the 0-1200 MPa range, the magnetization of the material decreases and its critical temperature shifts to lower temperatures, reaching T(C) = 7.5 K at 1200 MPa. Pressure-dependent Raman and Mossbauer spectroscopy measurements show that this striking behavior is due to the isomerization of some Cr(III)-C[triple bond]N-Fe(II) linkages to the Cr(III)-N[triple bond]C-Fe(II) form. As a result, the ligand field around the iron(II) centers increases, and the diamagnetic low-spin state is populated. As the number of diamagnetic centers in the cubic lattice increases, the net magnetization and critical temperature of the material decrease considerably. The phenomenon is reversible: releasing the pressure restores the magnetic properties of the original material. However, we have found that under more severe pressure conditions, a metastable sample containing 22% Cr(III)-N[triple bond]C-Fe(II) linkages can be obtained. X-ray absorption spectroscopy and magnetic circular dichroism of this metastable sample confirm the linkage isomerization process.
Subject(s)
Chromium Compounds/chemistry , Cyanides/chemistry , Iron Compounds/chemistry , Magnetics , Pressure , Water/chemistry , X-Rays , Crystallization , Isomerism , Spectrum Analysis , Temperature , X-Ray DiffractionABSTRACT
A pressure-induced linkage isomerization of the cyanide anion has been observed in single crystals of a chromium(III)-iron(II) Prussian blue analogue of formula K0.4Fe4[Cr(CN)6]2.8 square1.2.16H2O (1). Upon application of pressure in the 0-1200 MPa range, the cyanide ligand rotates and becomes C-bonded to the iron(II) cations, leading to a stabilization of their diamagnetic low-spin states. The result is a decrease of magnetization and magnetic ordering temperatures from TC = 19 K at ambient pressure to 13 K at 1200 MPa. The initial magnetic properties can be restored on pressure release. The reversible movement of cyanide in the solid state can be exploited as a switch of the magnetic interaction at the molecular level.