ABSTRACT
The Ni-TiO2 and Ni-CeO2 composite coatings with varying hydrophilic/hydrophobic characteristics were fabricated by the electrodeposition method from a tartrate electrolyte at ambient temperature. To meet the requirements of tight regulation by the European Chemicals Agency classifying H3BO3 as a substance of very high concern, Rochelle salt was utilized as a buffer solution instead. The novelty of this study was to implement a simple one-step galvanostatic electrodeposition from the low-temperature electrolyte based on a greener buffer compared to traditionally used, aiming to obtain new types of soft-matrix Ni, Ni-CeO2, and Ni-TiO2 coatings onto steel or copper substrates. The surface characteristics of electrodeposited nickel composites were evaluated by SEM, EDS, surface contact angle measurements, and XPS. Physiochemical properties of pure Ni, Ni-CeO2, and Ni-TiO2 composites, namely, wear resistance, microhardness, microroughness, and photocatalytic activity, were studied. Potentiodynamic polarization, EIS, and ICP-MS analyses were employed to study the long-term corrosion behavior of coatings in a 0.5 M NaCl solution. Superior photocatalytic degradation of methylene blue, 96.2% after 6 h of illumination, was achieved in the case of Ni-TiO2 composite, while no substantial change in the photocatalytic behavior of the Ni-CeO2 compared to pure Ni was observed. Both composites demonstrated higher hardness and wear resistance than pure Ni. This study investigates the feasibility of utilizing TiO2 as a photocatalytic hydrophilicity promoter in the fabrication of composite coatings for various applications.
ABSTRACT
Two 4,4'-(hexafluoroisopropylidene)diphthalic anhydride-based thermosetting polyimide formulations with varied amounts of crosslinking sites were compared to understand the influence of crosslinking density on fracture toughness, glass transition temperature and thermal oxidative stability. The thermal and mechanical properties of both materials were investigated through a series of single-edge notched beams, differential scanning calorimetry, dilatometry, weight loss, light optical microscopy and nanoindentation experiments. It was found out that the reduced crosslinking resulted in slightly increased fracture toughness but decreased the Tg of the material. No significant difference could be observed in the thermal oxidative stability with the experimental techniques considered.
ABSTRACT
Wheat gluten biopolymers generally become excessively rigid when processed without plasticisers, while the use of plasticisers, on the other hand, can deteriorate their mechanical properties. As such, this study investigated the effect of carbon black (CB) as a filler into glycerol-plasticised gluten to prepare gluten/CB biocomposites in order to eliminate the aforementioned drawback. Thus, biocomposites were manufactured using compression moulding followed by the determination of their mechanical, morphological, and chemical properties. The filler content of 4 wt% was found to be optimal for achieving increased tensile strength by 24%, and tensile modulus by 268% along with the toughness retention based on energy at break when compared with those of glycerol-plasticised gluten. When reaching the filler content up to 6 wt%, the tensile properties were found to be worsened, which can be ascribed to excessive agglomeration of carbon black at the high content levels within gluten matrices. Based on infrared spectroscopy, the results demonstrate an increased amount of ß-sheets, suggesting the formation of more aggregated protein networks induced by increasing the filler contents. However, the addition of fillers did not improve fire and water resistance in such bionanocomposites owing to the high blend ratio of plasticiser to gluten.