Direct Ink Writing of Low-Concentration MXene/Aramid Nanofiber Inks for Tunable Electromagnetic Shielding and Infrared Anticounterfeiting Applications.

MXene inks offer a promising avenue for the scalable production and customization of printing electronics. However, simultaneously achieving a low solid content and printability of MXene inks, as well as mechanical flexibility and environmental stability of printed objects, remains a challenge. In this study, we overcame these challenges by employing high-viscosity aramid nanofibers (ANFs) to optimize the rheology of low-concentration MXene inks. The abundant entangled networks and hydrogen bonds formed between MXene and ANF significantly increase the viscosity and yield stress up to 103 Pa·s and 200 Pa, respectively. This optimization allows the use of MXene/ANF (MA) inks at low concentrations in direct ink writing and other high-viscosity processing techniques. The printable MXene/ANF inks with a high conductivity of 883.5 S/cm were used to print shields with customized structures, achieving a tunable electromagnetic interference shielding effectiveness (EMI SE) in the 0.2-48.2 dB range. Furthermore, the MA inks exhibited adjustable infrared (IR) emissivity by changing the ANF ratio combined with printing design, demonstrating the application for infrared anticounterfeiting. Notably, the printed MXene/ANF objects possess outstanding mechanical flexibility and environmental stability, which are attributed to the reinforcement and protection of ANF. Therefore, these findings have significant practical implications as versatile MXene/ANF inks can be used for customizable, scalable, and cost-effective production of flexible printed electronics.

Enhanced Electromagnetic Shielding and Thermal Management Properties in MXene/Aramid Nanofiber Films Fabricated by Intermittent Filtration.

High-efficiency electromagnetic interference (EMI) shielding and heat dissipation synergy materials with flexible, robust, and environmental stability are urgently demanded in next-generation integration electronic devices. In this work, we report the lamellar MXene/Aramid nanofiber (ANF) composite films, which establish a nacre-like structure for EMI shielding and heat dissipation by using the intermittent filtration strategy. The MXene/ANF composite film filled with 50 wt % MXene demonstrates enhanced mechanical properties with a strength of 230.5 MPa, an elongation at break of 6.2%, and a toughness of 11.8 MJ·m3 (50 wt % MXene). These remarkable properties are attributed to the hydrogen bonding and highly oriented structure. Furthermore, due to the formation of the MXene conductive network, the MXene/ANF composite film shows an outstanding conductivity of 624.6 S/cm, an EMI shielding effectiveness (EMI SE) of 44.0 dB, and a superior specific SE value (SSE/t) of 18847.6 dB·cm2/g, which is better than the vacuum filtration film. Moreover, the MXene/ANF composite film also shows a great thermal conductivity of 0.43 W/m·K. The multifunctional MXene/ANF composite films with high-performance EMI shielding, heat dissipation, and joule heating show great potential in the field of aerospace, military, microelectronics, microcircuit, and smart wearable electronics.