ABSTRACT
The present research work shows the effect on the carbonation of Portland cement-based mortars (PC) with the addition of green materials, specifically residues from two groups: agricultural and industrial wastes, and minerals and fibres. These materials have the purpose of helping with the waste disposal, recycling, and improving the durability of concrete structures. The specimens used for the research were elaborated with CPC 30R RS, according to the Mexican standard NMX-C-414, which is equivalent to the international ASTM C150. The aggregates were taken from the rivers Lerma and Huajumbaro, in the State of Michoacan, Mexico, and the water/cement relation was 1:1 in weight. The carbonation analyses were performed with cylinder specimens in an accelerated carbonation test chamber with conditions of 65 +/- 5% of humidity and 25 +/- 2 °C temperature. The results showed that depending on the PC substitutions, the carbonation front advance of the specimens can increase or decrease. It is highlighted that the charcoal ashes, blast-furnace slags, and natural perlite helped to reduce the carbonation advance compared to the control samples, consequently, they contributed to the durability of concrete structures. Conversely, the sugarcane bagasse ash, brick manufacturing ash, bottom ash, coal, expanded perlite, metakaolin, and opuntia ficus-indica dehydrated fibres additions increased the velocity of carbonation front, helping with the sequestration of greenhouse gases, such as CO2, and reducing environmental pollution.
ABSTRACT
In this work, sugarcane bagasse fiber, a waste product of agroindustry, was added to mortar mixes at different proportions looking to seal porosities so as to improve the resistance of concrete to carbonation and to improve its mechanical properties. To evaluate the behavior of bagasse fibers in the alkaline media typical of mortars, bagasse fibers were subjected to solutions with alkaline pH values, and their chemical structure and morphological behavior was evaluated using FTIR (Fourier transform infrared spectroscopy) and SEM (Scanning Electron Microscopy). Using mortar cylinders in an accelerated carbonation chamber to obtain results in short lapses, the compressive strength and the carbonation were evaluated. The FTIR analysis results indicate that pH values of 11 and 12 causes a delignification, while at pH 9 and 10, a swelling of the molecule occurs because of the addition of hydroxyl ions, behavior that is confirmed with SEM images. A clear effect of the fiber addition on the performance of concrete was observed as the carbonation front of 35 mm for the sample without fibers was reduced to 2 mm for the sample with 2% fiber addition, resulting in an increase of 5 MPa in compressive strength. These results indicate that in the range of mortar pH, chemical changes occured over the sugarcane surface that could cause the growth of fibers and could partially seal the porosity in the mortars, thus enhancing its performance.
ABSTRACT
Hybrid organic-inorganic materials based on cellulose matrix and silica particles are obtained from wastes of the local paper recycling mill and sugarcane mill as renewable secondary raw materials. The performance comparison of these hybrid materials made from secondary raw materials against the materials made from pure, raw sources is discussed. The Fourier transform infrared spectra show that cellulose features prevail even at 43 wt% silica nanoparticles in the hybrid materials. Such a high content of silica originated from sugarcane bagasse ash and hollow glass microspheres contributes to the high thermal stability of the final composites, as seen by thermogravimetric analysis with very low water absorption. This one-step approach of biobased hybrid materials represents an excellent way to produce high-performance materials with high content of inorganic nanoparticles for a wide variety of applications like energy efficient building material completely cement-free.