ABSTRACT
This study investigated the self-healing properties of PA6/COC blends, in particular, the impact of three compatibilizers on the rheological, microstructural, and thermomechanical properties. Dynamic rheological analysis revealed that ethylene glycidyl methacrylate (E-GMA) played a crucial role in reducing interfacial tension and promoting PA6 chain entanglement with COC domains. Mechanical tests showed that poly(ethylene)-graft-maleic anhydride (PE-g-MAH) and polyolefin elastomer-graft-maleic anhydride (POE-g-MAH) compatibilizers enhanced elongation at break, while E-GMA had a milder effect. A thermal healing process at 140 °C for 1 h was carried out on specimens broken in fracture toughness tests, performed under quasi-static and impact conditions, and healing efficiency (HE) was evaluated as the ratio of critical stress intensity factors of healed and virgin samples. All the compatibilizers increased HE, especially E-GMA, achieving 28.5% and 68% in quasi-static and impact conditions, respectively. SEM images of specimens tested in quasi-static conditions showed that all the compatibilizers induced PA6 plasticization and crack corrugation, thus hindering COC flow in the crack zone. Conversely, under impact conditions, E-GMA led to the formation of brittle fractures with planar surfaces, promoting COC flow and thus higher HE values. This study demonstrated that compatibilizers, loading mode, and fracture surface morphologies strongly influenced self-healing performance.
ABSTRACT
The development of fully renewable and biodegradable composites for short-term applications was pursued by combining a compatibilized poly(lactic acid) (PLA)/poly(butylene succinate-co-adipate) (PBSA) (60:40 wt:wt) blend with coffee silver skin (CSS), an industrial byproduct from coffee processing. An epoxy-based reactive agent (Joncryl ADR-4468) was added as a compatibilizer. CSS was incorporated at 5, 10, and 20 wt% in the blend both in the as-received state and after a simple thermal treatment in boiling water, which was performed to mitigate the negative impact of this filler on the rheological and mechanical properties of the blend. The CSS treatment effectively increased the filler degradation temperature of 30-40 °C, enabling stable melt processing of the composites. It also improved filler-matrix adhesion, resulting in enhanced impact properties (up to +172% increase in impact energy compared to the untreated filler). Therefore, treated CSS demonstrated potential as an effective green reinforcement for PLA/PBSA blends for rigid packaging applications. Future works will focus on studying suitable surface modification of CSS to further increase the interfacial interaction and the tensile quasi-static properties, to fully exploit the capabilities of this renewable material toward the development of eco-friendly composites.
ABSTRACT
This work aims to produce poly(lactic acid) (PLA)/poly(alkylene furanoate)s (PAF)s fiber blends for textile applications and evaluates their microstructural, chemical, thermal, and mechanical properties. The work focuses on two PAFs with very different alkyl chain lengths, i.e., poly(ethylene 2,5-furandicarboxylate) (PEF) and poly(dodecamethylene 2,5-furandicarboxylate) (PDoF), which were blended in solution at various concentrations (in the range 2.5-10 wt %) with PLA, wet spun, and subsequently drawn. Light optical micrographs highlight that PLA/PEF blends present large and concentrate PEF domains, whereas PLA/PDoF blends show small and homogeneously distributed PDoF domains. The blends appear to be immiscible, which is confirmed also by scanning electron microscopy (SEM), Fourier-Transform Infrared (FT-IR) spectroscopy, and differential scanning calorimetry (DSC). Thermogravimetric analysis (TGA) highlights that the addition of the PAFs improves the thermal stability of the fibers. The drawing process, which was carried out at 80 °C with a heat setting step at 95 °C and at three draw ratios, improves the mechanical properties of the fibers upon the addition of the PAFs. The results obtained in this study are promising and may serve as a basis for future investigations on these novel bio-based fiber blends, which can contribute to increase the environmental sustainability of industrial textiles.
ABSTRACT
Drawing is a well-established method to improve the mechanical properties of wet-spun fibers, as it orients the polymer chains, increases the chain density, and homogenizes the microstructure. This work aims to investigate how drawing variables, such as the draw ratio, drawing speed, and temperature affect the elastic modulus (E) and the strain at break (εB) of biobased wet-spun fibers constituted by neat polylactic acid (PLA) and a PLA/poly(dodecamethylene 2,5-furandicarboxylate) (PDoF) (80/20 wt/wt) blend. Drawing experiments were conducted with a design of experiment (DOE) approach following a 24 full factorial design. The results of the quasi-static tensile tests on the drawn fibers, analyzed by the analysis of variance (ANOVA) and modeled through the response surface methodology (RSM), highlight that the presence of PDoF significantly lowers E, which instead is maximized if the temperature and draw ratio are both low. On the other hand, εB is enhanced when the drawing is performed at a high temperature. Finally, a genetic algorithm was implemented to find the optimal combination of drawing parameters that maximize both E and εB. The resulting Pareto curve highlights that the temperature influences the mechanical results only for neat PLA fibers, as the stiffness increases by drawing at lower temperatures, while optimal Pareto points for PLA/PDoF fibers are mainly determined by the draw ratio and the draw rate.