ABSTRACT
The goal of this stydy was to explore the potential of the enhanced corrosion resistance of Ti(N,O) cathodic arc evaporation-coated 304L stainless steel using oxide nano-layers deposited by atomic layer deposition (ALD). In this study, we deposited Al2O3, ZrO2, and HfO2 nanolayers of two different thicknesses by ALD onto Ti(N,O)-coated 304L stainless steel surfaces. XRD, EDS, SEM, surface profilometry, and voltammetry investigations of the anticorrosion properties of the coated samples are reported. The amorphous oxide nanolayers homogeneously deposited on the sample surfaces exhibited lower roughness after corrosion attack compared to the Ti(N,O)-coated stainless steel. The best corrosion resistance was obtained for the thickest oxide layers. All samples coated with thicker oxide nanolayers augmented the corrosion resistance of the Ti(N,O)-coated stainless steel in a saline, acidic, and oxidising environment (0.9% NaCl + 6% H2O2, pH = 4), which is of interest for building corrosion-resistant housings for advanced oxidation systems such as cavitation and plasma-related electrochemical dielectric barrier discharge for breaking down persistent organic pollutants in water.
ABSTRACT
In this paper, cellulose nanocrystals (CNCs) were isolated from the cellulose extracted from cocoa pod husk waste, followed by characterization using XRD, FT-IR, TGA, SEM and TEM to determine its crystallinity, structural properties, thermal characteristics, morphology and dimensions respectively. The result revealed that the cocoa pod husk amorphous segments containing hemicelluloses and lignin were extensively removed with increasing chemical treatments leading to increased purity, crystallinity index and thermal stability of the extracted materials. The diameter, length and crystallinity index of the CNC isolated from the CPH are 10-60 nm, 41-155 nm and 67.60% respectively.
ABSTRACT
This study reports on formulations and conditions for producing fly ash-based geopolymers with a view to showing that the compressive strength required for construction applications can be obtained without the addition of aggregates, sand, and/or cement. It was shown in a series of experiments constituting at least 73% fly ash that a compressive strength of up to 90 MPa can be obtained depending on the curing conditions. While high alkalinity resulted in stronger materials, the results showed about 40% savings in CO2 emissions without using sand and cement. Such materials are suited for construction applications with minimal environmental impact.
ABSTRACT
The development of durable photocatalytic supports resistant in harsh environment has become challenging in advanced oxidation processes (AOPs) focusing on water and wastewater remediation. In this study, stainless steel (SS), SS/Ti (N,O) and SS/Cr-N/Cr (N,O) anticorrosion layers on SS meshes were dip-coated with sol gel synthesised C-N-TiO2 photo catalysts pyrolysed at 350 °C for 105 min, using a heating rate of 50 °C/min under N2 gas. The supported C-N-TiO2 films were characterised by scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and Raman spectroscopy. The results showed that C-N-TiO2 was successfully deposited on anticorrosion coated SS supports and had different morphologies. The amorphous C and TiO2 were predominant in C-N-TiO2 over anatase and rutile phases on the surface of SS and anticorrosion supports. The C-N-TiO2 coated films showed enhanced photocatalytic activity for the decolouration of O.II dye under both solar and UV radiation. The fabricated C-N-TiO2 films showed significant antibacterial activities in the dark as well as in visible light. Herein, we demonstrate that SS/Ti(N,O) and SS/Cr-N/Cr(N,O) anticorrosion coatings are adequate photocatalytic and corrosion resistant supports. The C-N-TiO2 photo catalytic coatings can be used for water and wastewater decontamination of pollutants and microbes.