ABSTRACT
Aqueous solutions of oxalato- and citrato-VO(2+) complexes are prepared, and their ligand exchange reaction is investigated as a function of the amount of citrate present in the aqueous solution via continuous-wave electron paramagnetic resonance (CW EPR) and hyperfine sublevel correlation (HYSCORE) spectroscopy. With a low amount of citrate, monomeric cis-oxalato-VO(2+) complexes occur with a distorted square-pyramidal geometry. As the amount of citrate increases, oxalate is gradually exchanged for citrate. This leads to (i) an intermediate situation of monomeric VO(2+) complexes with a mix of oxalate/citrate ligands and (ii) a final situation of both monomeric and dimeric complexes with exclusively citrato ligands. The monomeric citrato-VO(2+) complexes dominate (abundance > 80%) and are characterized by a 6-fold chelation of the vanadium(IV) ion by 4 RCO2(-) ligands at the equatorial positions and a H2O/R-OH ligand at the axial position. The different redox stabilities of these complexes, relative to that of dissolved O2 in the aqueous solution, is analyzed via (51)V NMR. It is shown that the oxidation rate is the highest for the oxalato-VO(2+) complexes. In addition, the stability of the VO(2+) complexes can be drastically improved by evacuation of the dissolved O2 from the solution and subsequent storage in a N2 ambient atmosphere. The vanadium oxide phase formation process, starting with the chemical solution deposition of the aqueous solutions and continuing with subsequent processing in an ambient 0.1% O2 atmosphere, differs for the two complexes. The oxalato-VO(2+) complexes turn into the oxygen-deficient crystalline VO2 B at 400 °C, which then turns into crystalline V6O13 at 500 °C. In contrast, the citrato-VO(2+) complexes form an amorphous film at 400 °C that crystallizes into VO2 M1 and V6O13 at 500 °C.
ABSTRACT
An aqueous precursor solution, containing citrato-VO(2+) complexes, is synthesized for the formation of monoclinic VO2. With regard to the decomposition of the VO(2+) complexes towards vanadium oxide formation, it is important to gain insights into the chemical structure and transformations of the precursor during synthesis and thermal treatment. Hence, the conversion of the cyclic [V4O12](4-) ion to the VO(2+) ion in aqueous solution, using oxalic acid as an acidifier and a reducing agent, is studied by (51)Vanadium nuclear magnetic resonance spectroscopy. The citrate complexation of this VO(2+) ion and the differentiation between a solution containing citrato-oxalato-VO(2+) and citrato-VO(2+) complexes are studied by electron paramagnetic resonance and Fourier transform infra-red spectroscopy. In both solutions, the VO(2+) containing complex is mononuclear and has a distorted octahedral geometry with a fourfold R-CO2(-) ligation at the equatorial positions and likely a fifth R-CO2(-) ligation at the axial position. Small differences in the thermal decomposition pathway between the gel containing citrato-oxalato-VO(2+) complexes and the oxalate-free gel containing citrato-VO(2+) complexes are observed between 150 and 200 °C in air and are assigned to the presence of (NH4)2C2O4 in the citrato-oxalato-VO(2+) solution. Both precursor solutions are successfully used for the formation of crystalline vanadium oxide nanostructures on SiO2, after thermal annealing at 500 °C in a 0.1% O2 atmosphere. However, the citrato-oxalato-VO(2+) and the oxalate-free citrato-VO(2+) solution result in the formation of monoclinic V6O13 and monoclinic VO2, respectively.
ABSTRACT
An aqueous deposition process for V(6)O(13) films is developed whereby the vanadium oxidation state is continuously controlled throughout the entire process. In the precursor stage, a controlled wet chemical reduction of the vanadium(V) source with oxalic acid is achieved and monitored by (51)Vanadium Nuclear Magnetic Resonance ((51)V-NMR) and Ultraviolet-Visible (UV-Vis) spectroscopy. The resulting vanadium(IV) species in the aqueous solution are identified as mononuclear citrato-oxovanadate(IV) complexes by Electron Paramagnetic Resonance (EPR) and Fourier Transform Infra-Red (FTIR) spectroscopy. This precursor is successfully employed for the deposition of uniform, thin films. The optimal deposition and annealing conditions for the formation of crystalline V(6)O(13), including the control of the vanadium oxidation state, are determined through an elaborate study of processing temperature and O(2) partial pressure. To ensure a sub 100 nm adjustable film thickness, a non-oxidative intermediate thermal treatment is carried out at the end of each deposition cycle, allowing maximal precursor decomposition while still avoiding V(IV) oxidation. The resulting surface hydrophilicity, indispensable for the homogeneous deposition of the next layer, is explained by an increased surface roughness and the increased availability of surface vanadyl groups. Crystalline V(6)O(13) with a preferential (002) orientation is obtained after a post deposition annealing in a 0.1% O(2) ambient for thin films with a thickness of 20 nm.