ABSTRACT
The deformation behavior of duplex stainless steel under tension and bending, accompanied by a pulsed current and when heated by an external source, is investigated. The stress-strain curves are compared at the same temperatures. The contribution to the decrease in flow stresses is greater when using a multi-pulse current at the same temperature, compared to external heating. This confirms the presence of an electroplastic effect. An increase in the strain rate by an order of magnitude reduces the contribution of the electroplastic effect from single pulses to the reduction in flow stresses by 20%. An increase in the strain rate by an order of magnitude reduces the contribution of the electroplastic effect from single pulses to the reduction in flow stresses by 20%. However, in the case of a multi-pulse current, the strain rate effect is not observed. Introducing a multi-pulse current during bending reduces the bending strength by a factor of two and the springback angle to 6.5.
ABSTRACT
In this work, the composition of an electrolyte was selected and optimized to induce the formation of hydroxyapatite during Plasma electrolytic oxidation (PEO) treatment on an AZ31 alloy for application in bioabsorbable implants. In detail, the PEO process, called PEO-BIO (Plasma Electrolytic Oxidation-Biocompatible), was performed using a silicate-phosphate-based electrolyte with the addition of calcium oxide in direct-current mode using high current densities and short treatment times. For comparison, a known PEO process for producing anticorrosive coatings, called standard, was applied on the same alloy. The coatings were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and XPS analyses. The corrosion performance was evaluated in simulated body fluid (SBF) at 37 °C. The coating produced on the PEO-BIO sample was porous and thicker than the standard PEO one, with zones enriched in Ca and P. The XRD analysis showed the formation of hydroxyapatite and calcium oxides in addition to magnesium-silicon oxide and magnesium oxide in the PEO-BIO sample. The corrosion resistance of PEO-BIO sample was comparable with that of a traditional PEO treated sample, and higher than that of the untreated alloy.
ABSTRACT
A novel high silicon austempered (AHS) steel has been studied in this work. The effect of different austenitizing temperatures, in full austenitic and biphasic regime, on the final microstructure was investigated. Specimens were austenitized at 780 °C, 830 °C, 850 °C and 900 °C for 30 min and held isothermally at 350 °C for 30 min. A second heat treatment route was performed which consisted of austenitizing at 900 °C for 30 min and austempering at 300 °C, 350 °C and 400 °C for 30 min. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) have been used to evaluate the microstructural evolution. These techniques revealed that the microstructures were composed of carbide-free bainite, ferrite, martensite and retained austenite (RA) in different volume fractions (Vγ). An aqueous borate buffer solution with 0.3 M H3BO3 and 0.075 M Na2B4O7∂10H2O (pH = 8.4) was used for corrosion tests in order to evaluate the influence of the different volume fractions of retained austenite on the corrosion properties of the specimens. The results showed that when increasing the austenitization temperatures, the volume fractions of retained austenite reached a maximum value at 850 °C, and decrease at higher temperatures. The corrosion properties were investigated after 30 min and 24 h immersion by means of potentiodynamic polarization (after 30 min) and electrochemical impedance spectroscopy (after both 30 min and 24 h) tests. The corrosion resistance of the samples increased with increases in the volume fraction of retained austenite due to lower amounts of residual stresses.